Precipitation in Al-Mg solid solution prepared by solidification under high pressure

Jinchuan Jie,Hongwei Wang,Chunming Zou,Z. J. Wei,Tingju Li

DOI: https://doi.org/10.1016/j.matchar.2013.10.023

IF: 4.537

2014-01-01

Materials Characterization

Abstract:The precipitation in Al–Mg solid solution containing 21.6at.%Mg prepared by solidification under 2GPa was investigated. The results show that the γ-Al12Mg17 phase is formed and the β′ phase cannot be observed in the solid solution during ageing process. The precipitation of γ and β phases takes place in a non-uniform manner during heating process, i.e. the γ and β phases are first formed in the interdendritic region, which is caused by the inhomogeneous distribution of Mg atoms in the solid solution solidified under high pressure. Peak splitting of X-ray diffraction patterns of Al(Mg) solid solution appears, and then disappears when the samples are aged at 423K for different times, due to the non-uniform precipitation in Al–Mg solid solution. The direct transformation from the γ to β phase is observed after ageing at 423K for 24h. It is considered that the β phase is formed through a peritectoid reaction of α+γ→β which needs the diffusion of Mg atoms across the interface of α/γ phases.