Abstract:In this paper, 2 atom % Al-doped ZnO (AZO) was prepared by the co-precipitation method together with sparking plasma sintering (SPS) treatment. The as-synthesized AZO powders show the morphology of hollow hexagonal towers, which result in a high porosity of 50.6% in the bulk sample consolidated by SPS sintering at 400 °C, and the porosity decreases gradually with increasing sintering temperature up to 1000 °C. Positron annihilation measurements reveal that even after sintering at 1000 °C, there are still a considerable number of small pores. A high electrical conductivity of 3 × 105 S m–1 is achieved at room temperature for the AZO sample sintered at 1000 °C, while the absolute values of Seebeck coefficient keep at relatively high values between 59 and 144 μV K–1 in the measurement temperature range of 27–500 °C, leading to a high power factor of 3.4 × 10–3 W m–1 K–2. On the other hand, the pores in AZO act as strong phonon scattering centers, and an extremely low thermal conductivity of 1.5 W m–1 K–1 measured at room temperature is obtained for AZO sintered at 400 °C. Due to the residual pores in the 1000 °C-sintered sample, the thermal conductivity is still relatively low. As a result, a maximum ZT of 0.275 measured at 500 °C is obtained in this sample, which is the highest ZT reported for ZnO around this temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16506?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16506</a>.Thermal gravity analysis for the Al-doped ZnO (Figure S1), TEM images of Al-doped ZnO sintered at different temperatures (Figure S2), and structural characterization and thermoelectric properties of undoped ZnO prepared by co-precipitation combined with SPS treatment (Figures S3–S5) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16506/suppl_file/am0c16506_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Sol–gel-hydrothermal Synthesis and Conductive Properties of Al-doped ZnO Nanopowders with Controllable Morphology

Surface Topography and Optical Properties of Al-doped ZnO Thin Films by Sol-gel Process

Solvothermal Synthesis and Conductive Properties of Nanorod-Constructed Al-doped ZnO Microflowers

Al-doped ZnO Nano-particles Synthesized by Liquid-Feed Flame Spray Pyrolysis and Electrical Conductivity Study

Preparation and Properties of Aluminum-Doped Zinc Oxide Ultrafine Powders

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Sol-gel Derived Al and Ga Co-Doped ZnO Nanoparticles: Structural, Morphological and Optical Investigation

Study on Aluminum Concentration on Optical and Electrical Properties of AZO Thin Films Fabricated by Ultrasonic Spray Pyrolysis

Synthesis of vertically aligned Al-doped ZnO nanorods array with controllable Al concentration

Preparation and characterization of solgel Al-doped ZnO thin films and ZnO nanowire arrays grown on Al-doped ZnO seed layer by hydrothermal method

Preparation And Properties For Aluminum-Doped Zinc Oxide Powders With The Coprecipitation Method

Significant Enhancement in the Thermoelectric Performance of Aluminum-Doped ZnO Tuned by Pore Structure

Effects of Al doping on the optical and electrical properties of pre-synthesized ZnO powders by solid state method

Preparation and Characterization of Aluminum Doped ZnO

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Highly Conductive Al-doped Tetra-Needle-like ZnO Whiskers Prepared by a Solid State Method

Study on Microstructure and Electrical Properties of ZnO:Al Thin Films Prepared by Sol-gel Method

Aluminum-doped zinc oxide nanoparticles with tunable near-infrared absorption/reflectance by a simple solvothermal process

High Dielectric Constant in Al-doped ZnO Ceramics Using High-Pressure Treated Powders

Controllable hydrothermal synthesis of Al-doped ZnO with different microstructures, growth mechanisms, and gas sensing properties

Characterizations and Application of Conductive ZAO Nanocrystals Prepared by Ultrasonic-Template Method