Abstract:In this paper, 2 atom % Al-doped ZnO (AZO) was prepared by the co-precipitation method together with sparking plasma sintering (SPS) treatment. The as-synthesized AZO powders show the morphology of hollow hexagonal towers, which result in a high porosity of 50.6% in the bulk sample consolidated by SPS sintering at 400 °C, and the porosity decreases gradually with increasing sintering temperature up to 1000 °C. Positron annihilation measurements reveal that even after sintering at 1000 °C, there are still a considerable number of small pores. A high electrical conductivity of 3 × 105 S m–1 is achieved at room temperature for the AZO sample sintered at 1000 °C, while the absolute values of Seebeck coefficient keep at relatively high values between 59 and 144 μV K–1 in the measurement temperature range of 27–500 °C, leading to a high power factor of 3.4 × 10–3 W m–1 K–2. On the other hand, the pores in AZO act as strong phonon scattering centers, and an extremely low thermal conductivity of 1.5 W m–1 K–1 measured at room temperature is obtained for AZO sintered at 400 °C. Due to the residual pores in the 1000 °C-sintered sample, the thermal conductivity is still relatively low. As a result, a maximum ZT of 0.275 measured at 500 °C is obtained in this sample, which is the highest ZT reported for ZnO around this temperature.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16506?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16506</a>.Thermal gravity analysis for the Al-doped ZnO (Figure S1), TEM images of Al-doped ZnO sintered at different temperatures (Figure S2), and structural characterization and thermoelectric properties of undoped ZnO prepared by co-precipitation combined with SPS treatment (Figures S3–S5) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16506/suppl_file/am0c16506_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Highly Conductive Al-doped Tetra-Needle-like ZnO Whiskers Prepared by a Solid State Method

Surface Topography and Optical Properties of Al-doped ZnO Thin Films by Sol-gel Process

Microstructure and Electrical Properties of Al-doped ZnO Thin Films

Effects of Al Doping on the Properties of ZnO Thin Films Deposited by Atomic Layer Deposition

Significant Enhancement in the Thermoelectric Performance of Aluminum-Doped ZnO Tuned by Pore Structure

Influence of Al Doping on the Properties of Zno Thin Films Grown by Atomic Layer Deposition

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Al-doped ZnO Nano-particles Synthesized by Liquid-Feed Flame Spray Pyrolysis and Electrical Conductivity Study

Electron doping of ALD-grown ZnO thin films through Al and P substitutions

High Annealing Stability of InAlZnO Nanofiber Field-Effect Transistors with Improved Morphology by Al Doping

Study on Microstructure and Electrical Properties of ZnO:Al Thin Films Prepared by Sol-gel Method

Effect of Al-doping on Crystallinity and Microstructure of ZnO:Al Thin Films

Tailoring of Optical and Electrical Properties of Transparent and Conductive Al-doped ZnO Films by Adjustment of Al Concentration

Preparation and characterization of Al-doped quasi-aligned ZnO submicro-rods

Studies on Morphology, Electrical and Optical Characteristics of Al-doped ZnO Thin Films Grown by Atomic Layer Deposition

Optimization of thermoelectric properties of Al-doped Zn1−xAlxO under high pressure and high temperature

Influence of Al Doping on the Structural, Optical, and Electrical Characteristics of ZnMn2O4

Growth behaviors and characteristics of low temperature spin-sprayed ZnO and Al-doped ZnO microstructures

Al doping to promote optical transmissibility of ZnO thin films

Study on Aluminum Concentration on Optical and Electrical Properties of AZO Thin Films Fabricated by Ultrasonic Spray Pyrolysis

Synthesis and Mechanism of 1D ZnO Based on Alkaline Dissolution‐Conversion Strategy of High Stable and Soluble Ɛ‐zn(oh)2