Abstract:One-dimensional (1-D) well-aligned zinc oxide (ZnO) nanorods (NRs) without and with aluminum (Al) dopants were triumphantly grown on conductive indium–tin-oxide glass substrates through a simple chemical bath deposition at low temperature in this study. The designed devices are also called the AZO-0 and AZO-1 samples. After annealing in a vacuum state (10 min, 600 °C), the optical properties of the nanostructures were explored via photoluminescence emission spectroscopy. Field-emission scanning electron microscopy, high-resolution transmission electron microscopy, and an X-ray diffraction spectrometer were used to investigate the surface nanostructures and crystalline properties of the NR arrays. It was seen that all nanostructures clearly showed a single-crystal property with hexagonal wurtzite shape and grew vertically on the substrate. The elemental content of the sample was checked by X-ray photoelectron spectroscopy and an energy-dispersive X-ray spectrometer. Additionally, nanogenerators (NGs) based on the 1-D AZO-0 and AZO-1 nanostructures were also fabricated and investigated. The copper tape was successfully utilized to combine nanostructures and electrodes for the NG device in an ultrasonic oscillator machine with a water chamber. As a result, it was found that the output power values of the AZO-1 NR NGs were higher than that of the AZO-0 NR NGs. The AZO-1 NRs revealed significantly superior conductive performance in NG devices and are promising candidates in future self-powered NG applications.

Solvothermal Synthesis and Conductive Properties of Nanorod-Constructed Al-doped ZnO Microflowers

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Synthesis of vertically aligned Al-doped ZnO nanorods array with controllable Al concentration

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Al-doped ZnO Nano-particles Synthesized by Liquid-Feed Flame Spray Pyrolysis and Electrical Conductivity Study

Fabrication of ZnO/Al2O3 core–shell nanostructures and crystalline Al2O3 nanotube

Arrays of ZnO Nanowires Fabricated by a Simple Chemical Solution Route

Morphology-Controllable synthesis of ZnO nano-/Micro- Structures by a solvothermal process in ethanol solution

Mechanism and Optimized Process Conditions of Forming One-Dimensional ZnO Nanorods with Al-Doping by Electrodeposition Method

Highly Uv Luminescent Zno Microtetrapod-On-Nanowire Hybrids

pH Controlled Nanostructure and Optical Properties of ZnO and Al-Doped ZnO Nanorod Arrays Grown by Microwave-Assisted Hydrothermal Method

Enhanced Nanogenerator Performances of 1-D Al-Doped ZnO Nanorod Arrays through Ultrasonic Wave Systems

Controllable Morphology of ZnO Nanostructures Via a Solvothermal Route

Synthesis and Characterization of Aligned ZnO Nanorods on Porous Aluminum Oxide Template.

Straight and Thin ZnO Nanorods: Hectogram-Scale Synthesis at Low Temperature and Cathodoluminescence.

Study on Aluminum Concentration on Optical and Electrical Properties of AZO Thin Films Fabricated by Ultrasonic Spray Pyrolysis

Fabrication and Morphology of ZnO Nanorods Array Prepared from Aqueous Solution under an Assisted Electrical Field

Room Temperature Synthesis of Branched ZnO Nanowires Array with Tunable Morphology

A Novel Low-Temperature Chemical Solution Route for Straight and Dendrite-Like Zno Nanostructures

Nitrogen-doped ZnO nanorods prepared by hydrothermal diffusion

ZnO Nanorod Arrays: Field-assisted Growth in Aqueous Solution and Field Emission Properties