Abstract:Ultralong ZnO nanowires with lengths of 20-80 mm and aspect ratios of 200-500 were synthesized within 15 minutes via a low-temperature hydrothermal method. With the assistance of sodium dodecyl sulfonate (SDSN) as the capping ligand, ZnO nanowires were formed by the initial nucleation of nanocrystals followed by the ligand-directed oriented attachment. Head-to-head attachment, side-by-side coalescence and nanocrystals attached to the surfaces were observed at different growth stages. ZnO microrods (lengths: 2-10 mm, diameters: 0.5 to 5 mm) were formed in the absence of SDSN. FT-IR spectra, XPS analysis and molecular dynamics simulations revealed that SDSN molecules were preferentially adsorbed onto the (100) planes rather than polar (001) planes, with their sulfonate groups coordinating with the surface zinc ions and possibly forming Zn-SO3 complexes. Such selective adsorption not only protected the initially nucleated ZnO nanocrystals from rapid aggregation, but also directed their subsequent self-assembly into highly-anisotropic nanowires. The as-prepared ZnO nanowires exhibited improved photoluminescence properties compared to the microrods. I-V characteristics indicated that the ZnO nanowires exhibited a much lower dark current, while an enhanced photocurrent upon 360 nm light illumination compared to the microrods. In addition, UV photodetectors using ZnO nanowires showed 27 times higher photo-sensitivity and 15.4/13.8 times higher rise/decay rates compared to those using ZnO microrods, which were attributed to the morphological effects in addition to the improved optical properties.

Highly Uv Luminescent Zno Microtetrapod-On-Nanowire Hybrids

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Largely Enhanced Efficiency In Zno Nanowire/P-Polymer Hybridized Inorganic/Organic Ultraviolet Light-Emitting Diode By Piezo-Phototronic Effect

ZnO Nanowire and $\hbox{ws}_{2}$ Nanotube Electronics

Hybrid Nanostructures of Au Nanocrystals and ZnO Nanorods: Layer-by-layer Assembly and Tunable Blue-Shift Band Gap Emission

Photoluminescence of ZrO2-ZnO Hybrid Nanotube Arrays Produced by Electrodeposition

4 Nm ZnO Nanocrystals Fabrication Through Electron Beam Irradiation on the Surface of a ZnO Nanoneedle Formed by Thermal Annealing

Photoluminescent Hierarchical Zno Micro‐flower and Its Surface Wettability

Synthesis Of Large-Scale Periodic Zno Nanorod Arrays And Its Blue-Shift Of Uv Luminescence

Preparation and Photoluminescence Properties of ZnO Nanowire/Nanorod Mix Arrays

Photoluminescence enhancement of ZnO nanowire arrays by atomic layer deposition of ZrO2 layers and thermal annealing.

Ligand-directed rapid formation of ultralong ZnO nanowires by oriented attachment for UV photodetectors

Morphological Characteristic and Photoluminescence Property of Zno Tetrapod Nanostructures Prepared by Self-Substrate Method

Rapid Synthesis and Photoluminescence of Novel ZnO Nanotetrapods

ZnO-NWs/metallic glass nanotube hybrid arrays: Fabrication and material characterization

Photoluminescence of ZnO Nanowires: A Review

High-performance UV photodetection of unique ZnO nanowires from zinc carbonate hydroxide nanobelts.

Controllable Growth of ZnO Nanorod Arrays on NiO Nanowires and Their High UV Photoresponse Current

Photoluminescence Characterization of Nanocrystalline ZnO Array

Facile synthesis and enhanced luminescent properties of ZnO/HfO2 core–shell nanowires

Direct resonant coupling of Al surface plasmon for ultraviolet photoluminescence enhancement of ZnO microrods.