Abstract:CO2 methanation was studied on Ni-based yttria-stabilised zirconia (Ni/YSZ) catalysts. The catalysts were prepared by the wet impregnation method, where the amount of Ni content was varied from 5% to 75%. Thereafter, the prepared catalysts were analysed by BET, XRD, SEM and H2-TPR. BET results showed an initial increase in the surface area with an increase in Ni loading, then a decrease after 30% Ni loading. The XRD results revealed that the Ni crystallite size increased as the Ni loading increased, while the H2-TPR showed a shift in reduction peak temperature to a higher temperature, indicating that the reducibility of the catalysts decreased as the Ni loading increased. The activity of the synthesised catalysts for CO2 methanation was studied by passing a mixture of H2, CO2 and N2 with a total flow of 135 mL min−1 and GHSV of 40,500 mL h−1 g−1 through a continuous flow quartz tube fixed-bed reactor (I.D. = 5.5 mm, wall thickness = 2 mm) containing 200 mg of the catalyst at a temperature range of 473 to 703 K under atmospheric pressure and a H2:CO2 ratio of 4. The tested Ni/YSZ catalysts showed an improvement in activity as the reaction temperature increased from 473 K to around 613 to 653 K, depending on the Ni loading. Beyond the optimum temperature, the catalyst’s activity started to decline, irrespective of the Ni loading. In particular, the 40% Ni/YSZ catalyst displayed the best performance, followed by the 30% Ni/YSZ catalyst. The improved activity at high Ni loading (40% Ni) was attributed to the increase in hydrogen coverage and improved site for both H2 and CO2 adsorption and activation.

Methane conversion to syngas over Ni/Y2O3 catalysts - Effects of calcination temperatures of Y2O3 on physicochemical properties and catalytic performance

Properties of Ni/Y2O3 and Its Catalytic Performance in Methane Conversion to Syngas

Effect of support texture properties on Ni-Fe/γ-Al_2O_3 catalyst structure and catalytic performance for CO methanation

Partial Oxidation Of Methane To Syngas Over Ni-Based Catalysts

Effect of Calcination Temperature on the Performance of the Ni@SiO2 Catalyst in Methane Dry Reforming

Investigating the Effect of Ni Loading on the Performance of Yttria-Stabilised Zirconia Supported Ni Catalyst during CO2 Methanation

Methanation of CO 2 over Y b-Promoted Ni/Al 2 O 3 Catalysts Prepared by Solution Combustion

Tuning Metal–Support Interactions on Ni/Al2O3 Catalysts to Improve Catalytic Activity and Stability for Dry Reforming of Methane

Study on Methanation Performance of Biomass Gasification Syngas Based on a Ni/Al2O3 Monolithic Catalyst

Methanation of CO2 over Ni/clay: Effects of Calcination Temperature on Catalyst Properties and Reaction Intermediates Formed

Effects of Calcination Temperature on the Catalytic Performance of Ni-Al2 O3 Catalyst

Dry reforming of methane on Ni/mesoporous-Al2O3 catalysts: Effect of calcination temperature

Catalytic Methanation of Syngas over Ni-based Catalysts with Different Supports

Effect of Ni Precipitation Method on CO Methanation over Ni/TiO 2 Catalysts

Effect of Ni Precipitation Method on CO Methanation over Ni/TiO2 Catalysts

Catalytic Partial Oxidation of Methane to Syngas over Ca-Decorated-Al2o3-Supported Ni and Nib Catalysts

Insight and comprehensive study of Ni-based catalysts supported on various metal oxides for CO2 methanation

Effect of Calcination Temperature on Characteristics and Performance of Ni/MgO Catalyst for CO2 Reforming of Toluene

Effects Of Hydrothermal Conditions Of Zro2 On Catalyst Properties And Catalytic Performances Of Ni/Zro2 In The Partial Oxidation Of Methane

Effect of the Calcination Temperature of LaNiO3 on the Structural Properties and Reaction Performance of Catalysts in the Steam Reforming of Methane

Physicochemical properties of Ni/γ-Al2O3-AlN and effects of AlN on catalytic performance of Ni/γ-Al2O 3-AlN in partial oxidation of methane