Abstract:Hydrotalcite-type solids of the form NiAl-R, where R refers to the ratio of Ni to Al (R = 2, 3, 5, 8, and 10), were successfully synthesized following co-precipitation method at pH = 12. The obtained solids were calcined at 800 °C, except for NiAl-R2 where calcination was performed at temperatures ranging between 300 and 800 °C. Following calcination, the resulting materials were evaluated for their catalytic activity and stability during the process of dry reforming of methane. Factors affecting the catalytic activity of the obtained materials such as the ratio R and calcination temperature were also studied. Prior to calcination, X-ray diffraction analyses clearly illustrated the typical hydrotalcite structure of the synthesized materials (when R ≤ 5). On the other hand, calcination at various temperatures prompted decomposition of all solids to form NiO, with exception to NiAl-R2, which upon calcinations at 800 °C was decomposed to form NiO and a second phase spinel containing NiAl2O4. The chemical composition of the obtained solids was determined by atomic absorption spectroscopy. Further characterization was performed using several techniques, including: surface area measurements (SBET), scanning electron microscopy, Fourier transform infrared spectroscopy and thermogravimetric analysis. The reducibility of nickel species was studied via temperature-programmed reduction. The catalytic performance of the as-prepared samples was studied for dry reforming of methane under atmospheric pressure at temperatures ranging between 400 and 700 °C. The catalytic activity of the designed substances highlighted the importance of molar ratios i.e. Ni2+/Al3+ on the success of the overall dry reforming of methane process. The catalytic activity of the synthesized materials was also found to be directly proportional to the ratio of Ni/Al as well as the calcination temperature, with exception to NiAl-R2 which was found to exhibit the highest activity of all. The latter observation was perhaps associated with the lower size of the crystalline particles in conjunction with the presence of a second phase containing NiAl2O4. In this study, it is shown that the calcination temperature has a significant effect on the catalytic property and the crystallite size of the metal.

Effect of Calcination Temperature on the Performance of the Ni@SiO2 Catalyst in Methane Dry Reforming

Nickel‐Catalyzed Dry Reforming of Methane Via Modulating the Zirconia Shapes

Tuning Metal–Support Interactions on Ni/Al2O3 Catalysts to Improve Catalytic Activity and Stability for Dry Reforming of Methane

Effect of the Calcination Temperature of LaNiO3 on the Structural Properties and Reaction Performance of Catalysts in the Steam Reforming of Methane

Effect of Calcination Temperature on Characteristics and Performance of Ni/MgO Catalyst for CO2 Reforming of Toluene

Effect of the Ni/Al ratio of hydrotalcite-type catalysts on their performance in the methane dry reforming process

CO2 Reforming with Methane Reaction over Ni@SiO2 Catalysts Coupled by Size Effect and Metal-Support Interaction

Dry reforming of methane on Ni/mesoporous-Al2O3 catalysts: Effect of calcination temperature

Methane conversion to syngas over Ni/Y2O3 catalysts - Effects of calcination temperatures of Y2O3 on physicochemical properties and catalytic performance

Effects of Calcination Temperature on the Catalytic Performance of Ni-Al2 O3 Catalyst

Impact of preparation method on nickel speciation and methane dry reforming performance of Ni/SiO2 catalysts

Methanation of CO2 over Ni/clay: Effects of Calcination Temperature on Catalyst Properties and Reaction Intermediates Formed

Effect of Calcination Temperature on Cu-Modified Ni Catalysts Supported on Mesocellular Silica for Methane Decomposition

Carbon Dioxide Reforming of Methane over Ni Supported SiO2: Influence of the Preparation Method on the Resulting Structural Properties and Catalytic Activity

Non-oxidative calcination enhances the methane dry reforming performance of Ni/CeO 2− x catalysts under thermal and photo-thermal conditions

How reduction temperature influences the structure of perovskite-oxide catalysts during the dry reforming of methane

Confining Ni and ceria in silica shell as synergistic multifunctional catalyst for methane dry reforming reaction

Ni/SiO2 Catalyst Prepared by Strong Electrostatic Adsorption for a Low-Temperature Methane Dry Reforming Reaction

Durable Ni/Mgo Catalysts For Co2 Reforming Of Methane: Activity And Metal-Support Interaction

Performance of supported nickel catalyst for reforming of CH 4 with CO 2 to syngas: I. Effect of preparation conditions and Ni loading

Effects of calcination temperature on physicochemical property and activity of CuSO4/TiO2 ammonia-selective catalytic reduction catalysts