Abstract:The catalysts for methane dry reforming were commonly confronted with the problems of metal component agglomeration and carbon deposition. The catalysts made by solid-phase synthesis could effectively overcome these problems. In this paper, methane dry reforming was catalyzed over activated carbon supported Ni-catalysts prepared by solid-phase synthesis. Through this method, the catalysts exhibited a uniform metal dispersion over the carrier, with particle size at the nanoscale of 4.69 nm. Catalytic performance of the prepared catalysts was tested, and the results showed that the catalysts could effectively catalyze methane dry reforming, due to little metal agglomeration and the balanced competition between carbon deposition and carbon consumption. In the catalytic performance testing initiated at 900 °C, the conversions of CH4 and CO2 were maintained at 80.3% and 97.5% after the testing, respectively. It was also noticed the syngas generated in the testing process had a favorable H2/CO ratio, at around 1. The syngas was considered to be beneficial to the synthesis of methanol, ammonia and oxygen-containing chemicals by Fischer-Tropsch process. It should be emphasized the reactant gases conversions presented an upward trend when the testing arrived at about 2 h, revealing an enhancement of catalyst activity. In totally, the catalysts prepared by solid-phase synthesis could avoid the agglomeration of active component and the serious carbon deposition, thus slowing down the catalyst deactivation. Through this work, it was demonstrated solid-phase method could open up new possibilities for the synthesis of highly active and stable catalysts for methane dry reforming.

Confining Ni and ceria in silica shell as synergistic multifunctional catalyst for methane dry reforming reaction

Design Dual Confinement Ni@S-1@SiO2 2 Catalyst with Enhanced Carbon Resistance for Methane Dry Reforming

Design Dual Confinement Ni@S-1@SiO2 Catalyst with Enhanced Carbon Resistance for Methane Dry Reforming

Reducing Carbon Deposition and Enhancing Reaction Stability by Ceria for Methane Dry Reforming over Ni@SiO2@CeO2 Catalyst

CO2 Reforming with Methane Reaction over Ni@SiO2 Catalysts Coupled by Size Effect and Metal-Support Interaction

Rational design of nickel-based catalyst coupling with combined methane reforming to steadily produce syngas

Ni/Ce0.9Eu0.1O1.95 with enhanced coke resistance for dry reforming of methane

Ni-Cu Alloy Nanoparticles Confined by Physical Encapsulation with SiO 2 and Chemical Metal-Support Interaction with CeO 2 for Methane Dry Reforming

Ceria-modified Nickel Supported on Porous Silica As Highly Active and Stable Catalyst for Dry Reforming of Methane

Unlocking exceptional diffusion of porous Ni@SiO 2 nanocapsule catalysts for enhanced dry reforming of methane

Confinement effects over Ni-based catalysts for methane dry reforming

Ceria engineering in nickel catalysts to improve CH 4 selectivity and yield for CO methanation

Sandwich‐Like Silica@Ni@Silica Multicore–Shell Catalyst for the Low‐Temperature Dry Reforming of Methane: Confinement Effect Against Carbon Formation

Confined High Dispersion of Ni Nanoparticles Derived from Nickel Phyllosilicate Structure in Silicalite-2 Shell for Dry Reforming of Methane with Enhanced Performance

Developing Silicalite-1 Encapsulated Ni Nanoparticles as Sintering-/Coking-Resistant Catalysts for Dry Reforming of Methane

CeO2 nanorod@NiPhy core‐shell catalyst for methane dry reforming: effect of simultaneous sintering prevention of CeO2 support and active Ni

Highly efficient and stable Ni/CeO2-SiO2 catalyst for dry reforming of methane: Effect of interfacial structure of Ni/CeO2 on SiO2

High Carbon-Resistance Ni@CeO2 Core–Shell Catalysts for Dry Reforming of Methane

Sintering resistant Ni nanoparticles exclusively confined within SiO2 nanotubes for CH4 dry reforming

Catalytic Performances of Ni/Mesoporous Sio2 Catalysts for Dry Reforming of Methane to Hydrogen

Methane dry reforming over activated carbon supported Ni-catalysts prepared by solid phase synthesis