Abstract:Mg-doped Ni nanoparticles with the hexagonal close-packed (hcp) and face-centered cubic (fcc) structure have been synthesized by sol–gel method sintered at different temperatures in argon atmosphere. The structure, morphology and magnetic properties of the samples were studied by X-ray diffraction, TEM, VSM magnetometers and Magnetic Property Measurement System (Quantum Design MPMS XL-7), respectively. X-ray diffraction and TEM results showed that Ni–Mg solid solution was formed with the single phase of hexagonal close-packed structure. When the temperature reached 450°C, a temperature-induced phase transform from hcp to fcc was observed. The average particle size of the sample with hcp structure evaluated by Scherrer equation was about 6.0nm. Moreover, the VSM results demonstrated the existence of ferromagnetic behavior in both synthesized hcp and fcc Mg-doped Ni nanoparticles. The saturation magnetization (Ms) of all the samples was below that of bulk Ni (54emu/g). Nevertheless, the magnetic measurement at 5000Oe field for the sample with hcp structure showed that the unsaturated magnetization in hcp Mg-doped Ni nanoparticles was much smaller than that of the fcc Mg-doped Ni nanoparticles. From the M–T curves, the blocking temperature (TB) of the hcp Mg-doped Ni nanoparticles was estimated to be 10K. It was also found that changes of the stress, particle size and structure during heat-treating had significant influences on the magnetic properties of the Mg-doped Ni nanoparticles.

Analysis of the precipitation process of secondary phase MgNi 2.5B2 and superconducting properties in Ni-doped MgB 2 bulk

Influence of Ni Addition on the Process of Phase Formation in MgB 2 Bulk

Observation of Flux Jump in (Mgb2)(0.96)ni-0.04 Superconductor Doped with Milled Ni Powders

Phase Formation and Superconductive Properties of Cu Doped MgB2 Sintered with Milled B Powder

Competition of the Nano-Inclusions and the Effects on Critical Current Density in Ni and Sic Co-Doped Mgb2 Bulks

Effects of Ball Milling on the Sintering Process and Superconducting Properties of $(\hbox{mgb}_{2})_{0.96}\hbox{ni}_{0.04}$ Bulks

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Effect of addition of nanoparticle TiO2/SiO2 on the superconducting properties of MgB2

Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder

A Study on the Electronic Structure, Superconductivity, and Optical Properties of Mgcni3

Superconducting properties and growth mechanism of layered structure in MgB 2 bulks with Cu/Y 2 O 3 co-doping

Superconducting Properties and Microstructure in MgB 2 Bulks, Wires and Tapes

Superconducting Properties of Y2o3/Sic Co-Doped Bulk Mgb2

The Synthesis of Lamellar Nano MgB2 Grains with Nanoimpurities, Flux Pinning Centers and Their Significantly Improved Critical Current Density

The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

Influence of Mg and B Stoichiometry on the Formation Behavior of MgB2 Phase

Effect of nanometer-sized B powder on phase formation of polycrystalline MgB2

Synthesis and Magnetic Properties of Mg-Doped Hexagonal Close-Packed Ni Nanoparticles

The Effect of Graphene Coated Si, Ti and Nb Additions on the Superconducting Properties of MgB 2 Bulks

Nanoparticles of the Superconductor MgB2: Structural Characterization and in Situ Study of Synthesis Kinetics