First-Principles Investigation of Mechanical and Electronic Properties of Mnni3 (m=zn, Mg, or Cd)
Chong Li,W. G. Chen,Fei Wang,S. F. Li,Q. Sun,Songyou Wang,Yu Jia
DOI: https://doi.org/10.1063/1.3156641
IF: 2.877
2009-01-01
Journal of Applied Physics
Abstract:Mechanical and electronic properties of an antiperovskite-type superconductor ZnNNi3 as well as its isostructural and isovalent counterparts MgNNi3 and CdNNi3 have been studied by using the first-principles calculations. Lattice constant a, bulk modulus B, elastic constants of cubic lattice (C-11, C-12, and C-44), compressibility K, shear modulus G, tetragonal shear modulus G', effective charges, as well as electronic structures of the three compounds have been calculated. The results show that the lattice constants of the three compounds have a relationship a (ZnNNi3) < a(MgNNi3) < a(CdNNi3), while on the contrary, the order of the bulk modulus is B(CdNNi3) < B(MgNNi3) < B(ZnNNi3), consisting with the tetragonal shear modulus G'. The neighboring Ni and N atoms are prone to form covalent bonds, while the M-Ni/N (M=Zn, Mg, or Cd) favor ionic nature. For the electronic structures, Ni 3d and the hybridization between Ni 3d and N 2p have the most contributions to the total density of states at the Fermi level [N(E-F)] for all the three compounds. Although the component of M in the compounds has very small contributions to the N(E-F), it may lead to a small shift in the bands near the Fermi level and therefore influence the values of N(E-F), which probably results in the ZnNNi3 superconductivity at T-C approximate to 3 K while the other two compounds show no indication of superconducting transition down to the temperature. (c) 2009 American Institute of Physics. [DOI: 10.1063/1.3156641]