Influence of Ni Addition on the Process of Phase Formation in MgB 2 Bulk

Qian Zhao,Yongchang Liu,Qi Cai

DOI: https://doi.org/10.1007/s00339-012-6812-y

2012-01-01

Abstract:Nickel is an important sheath material for the fabrication of MgB 2 wires. However, the effects of Ni doping on the phase formation and superconducting properties of MgB 2 remain controversial. In this work, Ni powder is selected for doping in MgB 2 bulk in order to examine the corresponding changes. Combining with the DSC analysis and in-situ XRD results, we find indications that the Ni powder reacted with Mg and B, forming MgNi 2.5 B 2 at 600°C. The ternary compound began to decompose at a temperature above 800°C. The reactive phase, MgNi 2.5 B 2 , acted as an obstacle to the supercurrent flow, creating weak links among the MgB 2 grain boundaries. However, it is found that the added Ni formed a eutectic liquid phase with Mg at 506°C. The liquid phase helps the formation of MgB 2 at low temperature, which not only increases the density of the sample, but also improves the grain connectivity. Consequently, the presence of Ni in the MgB 2 sample is not necessarily a disadvantage; it depends on the desired application.