Abstract:An ultrasonic vibration-assisted air-cooled stirring rod process (ACSR + UV) was used to efficiently prepare a large-volume semisolid slurry with a mass of more than 40 kg. A low-cost Al–Si–Fe–Mg–Cu–Zn die-casted alloy with high thermal conductivity, high plasticity and medium strength was developed. The alloy was used to manufacture large, thin-walled parts for 5G base stations by using the ACSR + UV rheological die-casting (ACSR + UV R-DC) process. Investigations were performed on the microstructure, porosity, mechanical properties, fracture behaviour and thermal conductivity of the ACSR + UV R-DC alloy, which was then compared to traditionally die-casted (T-DC) and ACSR R-DC alloys. The mechanisms for the microstructural refinement and enhancement of the mechanical and thermal conductivity performances of the ACSR + UV R-DC alloy were also analysed. The results showed that the ACSR + UV process increased the nucleation rate of the melt due to the increase in the nucleation area and the generation of cavitation bubbles. A radial- and an axial-forced convection was also generated inside the melt under the combined effects of acoustic flow and mechanical stirring, thereby homogenising the melt composition field and the temperature field. Therefore, the ACSR + UV R-DC process not only refined the primary α-Al (α1-Al), the eutectic silicon and the secondary α-Al (α2-Al), but also greatly improved the morphology and the distribution of the β-Al5FeSi phase. The mechanical properties of the ACSR + UV R-DC alloy were higher than those of the T-DC and the ACSR R-DC alloys. Compared to the T-DC alloy, the ultimate tensile strength, elongation and yield strength of the ACSR + UV R-DC alloy were increased by 34%, 122% and 19%, respectively. This was because the ACSR + UV R-DC technique gave the alloy the characteristics of high density, fine spherical α1-Al grain and a fine and uniform β-phase, which improved the fracture behaviour of the alloy. The thermal conductivity of the ACSR + UV R-DC alloy was 184 W/(m K), which was 10.2% and 3.4% higher than that of T-DC and ACSR R-DC alloys, respectively. This was because the refined eutectic silicon and β phases in the ACSR + UV R-DC alloy facilitated an easier electron flow through the eutectic region, and the decrease in porosity increased the effective area of heat conduction.

Microstructure and Mechanical Properties of Rheo-Diecast Hypereutectic Al–Si Alloy with 2%fe Assisted with Ultrasonic Vibration Process

Influence of Rheo-Diecasting Processing Parameters on Microstructure and Mechanical Properties of Hypereutectic Al–30%Si Alloy

Towards high performance Al–Si–Fe alloy castings via rheo-diecasting: Effect of injection velocity and heat treatment on microstructure evolution and property

Microstructure and Properties of Rheo-Diecast Al-20Si-2Cu-1Ni-0.4Mg Alloy with Direct Ultrasonic Vibration Process

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

Dry Sliding Wear Properties of Rheo-diecasting Hypereutectic Al-Si Alloy with High Iron Content

Synchronously Improving the Thermal Conductivity and Mechanical Properties of Al–Si–Fe–Mg–Cu–Zn Alloy Die Castings Through Ultrasonic-Assisted Rheoforming

Solidification behavior and enhanced properties of semi-solid Al–8Si–0.5Fe alloys fabricated by rheo-diecasting

Microstructure and mechanical properties of rheo-diecasted A390 alloy

Reinforcement of Hypereutectic Al-Si Alloys with Fe-Bearing Compounds and Si Particles Assisted with Ultrasonic Treatment

Microstructure and Properties of High Silicon Aluminum Alloy with 2% Fe Prepared by Rheo-Casting

Rheo-Diecasting of Magnesium Alloys

Influence of High Pressure and Manganese Addition on Fe-rich Phases and Mechanical Properties of Hypereutectic Al−Si Alloy with Rheo-Squeeze Casting

Microstructure Evolution and Mechanical Properties of Rheo-Processed ADC12 Alloy

Microstructure and property of rheocasting aluminum-alloy made with indirect ultrasonic vibration process

A novel rheological high pressure die-casting process for preparing large thin-walled Al–Si–Fe–Mg–Sr alloy with high heat conductivity, high plasticity and medium strength

Melt Superheating on the Microstructure and Mechanical Properties of Diecast Al-Mg-Si-Mn Alloy

New technique for preparing A356 alloy semisolid slurry and its rheo-diecast microstructure and properties

Microstructure and Mechanical Properties of Hypereutectic Al-Si Alloy with 2% Fe Prepared by Semi-Solid Process

Rheo-Processing of Near-Eutectic Adc12 Alloy

Microstructure and Properties of in Situ Si and Fe-rich Particles Reinforced Al Matrix Composites Assisted with Ultrasonic Vibration