Abstract:An ultrasonic vibration-assisted air-cooled stirring rod process (ACSR + UV) was used to efficiently prepare a large-volume semisolid slurry with a mass of more than 40 kg. A low-cost Al–Si–Fe–Mg–Cu–Zn die-casted alloy with high thermal conductivity, high plasticity and medium strength was developed. The alloy was used to manufacture large, thin-walled parts for 5G base stations by using the ACSR + UV rheological die-casting (ACSR + UV R-DC) process. Investigations were performed on the microstructure, porosity, mechanical properties, fracture behaviour and thermal conductivity of the ACSR + UV R-DC alloy, which was then compared to traditionally die-casted (T-DC) and ACSR R-DC alloys. The mechanisms for the microstructural refinement and enhancement of the mechanical and thermal conductivity performances of the ACSR + UV R-DC alloy were also analysed. The results showed that the ACSR + UV process increased the nucleation rate of the melt due to the increase in the nucleation area and the generation of cavitation bubbles. A radial- and an axial-forced convection was also generated inside the melt under the combined effects of acoustic flow and mechanical stirring, thereby homogenising the melt composition field and the temperature field. Therefore, the ACSR + UV R-DC process not only refined the primary α-Al (α1-Al), the eutectic silicon and the secondary α-Al (α2-Al), but also greatly improved the morphology and the distribution of the β-Al5FeSi phase. The mechanical properties of the ACSR + UV R-DC alloy were higher than those of the T-DC and the ACSR R-DC alloys. Compared to the T-DC alloy, the ultimate tensile strength, elongation and yield strength of the ACSR + UV R-DC alloy were increased by 34%, 122% and 19%, respectively. This was because the ACSR + UV R-DC technique gave the alloy the characteristics of high density, fine spherical α1-Al grain and a fine and uniform β-phase, which improved the fracture behaviour of the alloy. The thermal conductivity of the ACSR + UV R-DC alloy was 184 W/(m K), which was 10.2% and 3.4% higher than that of T-DC and ACSR R-DC alloys, respectively. This was because the refined eutectic silicon and β phases in the ACSR + UV R-DC alloy facilitated an easier electron flow through the eutectic region, and the decrease in porosity increased the effective area of heat conduction.

Solidification behavior and enhanced properties of semi-solid Al–8Si–0.5Fe alloys fabricated by rheo-diecasting

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

Enhanced strength-ductility synergy in a rheo-diecasting semi-solid aluminum alloy

Microstructure and Properties of Semi-solid Die Casting of High Silicon Aluminum Alloy with High Thermal Conductivity

Towards high performance Al–Si–Fe alloy castings via rheo-diecasting: Effect of injection velocity and heat treatment on microstructure evolution and property

Microstructure and Mechanical Properties of Rheo-Diecast Hypereutectic Al–Si Alloy with 2%fe Assisted with Ultrasonic Vibration Process

Performance of semi-solid slurry produced by twin-screw stirring mixer and rheo-diecasting process of AZ91D alloy

Synchronously Improving the Thermal Conductivity and Mechanical Properties of Al–Si–Fe–Mg–Cu–Zn Alloy Die Castings Through Ultrasonic-Assisted Rheoforming

Rheo-Processing of Near-Eutectic Adc12 Alloy

Influence of Rheo-Diecasting Processing Parameters on Microstructure and Mechanical Properties of Hypereutectic Al–30%Si Alloy

Microstructure and Properties of Rheo-Diecast Al-20Si-2Cu-1Ni-0.4Mg Alloy with Direct Ultrasonic Vibration Process

Study on Semisolid Rheo-Diecasting Process, Microstructure and Mechanical Properties of Mg-6Al-1Ca-0.5Sb Alloy with High Solid Fraction

Microstructure and Properties of High Silicon Aluminum Alloy with 2% Fe Prepared by Rheo-Casting

Study on a Semi-Solid Rheo-Diecasting Process With AZ91D Alloy Slurry

A novel rheological high pressure die-casting process for preparing large thin-walled Al–Si–Fe–Mg–Sr alloy with high heat conductivity, high plasticity and medium strength

Melt Superheating on the Microstructure and Mechanical Properties of Diecast Al-Mg-Si-Mn Alloy

Effect of Solidification Sequence on the Microstructure and Mechanical Properties of Die-Cast Al–11Si–2Cu–Fe Alloy

Microstructure and properties of rheo-diecasting wrought aluminum alloy with Sc additions

New technique for preparing A356 alloy semisolid slurry and its rheo-diecast microstructure and properties

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy