Abstract:An ultrasonic vibration-assisted air-cooled stirring rod process (ACSR + UV) was used to efficiently prepare a large-volume semisolid slurry with a mass of more than 40 kg. A low-cost Al–Si–Fe–Mg–Cu–Zn die-casted alloy with high thermal conductivity, high plasticity and medium strength was developed. The alloy was used to manufacture large, thin-walled parts for 5G base stations by using the ACSR + UV rheological die-casting (ACSR + UV R-DC) process. Investigations were performed on the microstructure, porosity, mechanical properties, fracture behaviour and thermal conductivity of the ACSR + UV R-DC alloy, which was then compared to traditionally die-casted (T-DC) and ACSR R-DC alloys. The mechanisms for the microstructural refinement and enhancement of the mechanical and thermal conductivity performances of the ACSR + UV R-DC alloy were also analysed. The results showed that the ACSR + UV process increased the nucleation rate of the melt due to the increase in the nucleation area and the generation of cavitation bubbles. A radial- and an axial-forced convection was also generated inside the melt under the combined effects of acoustic flow and mechanical stirring, thereby homogenising the melt composition field and the temperature field. Therefore, the ACSR + UV R-DC process not only refined the primary α-Al (α1-Al), the eutectic silicon and the secondary α-Al (α2-Al), but also greatly improved the morphology and the distribution of the β-Al5FeSi phase. The mechanical properties of the ACSR + UV R-DC alloy were higher than those of the T-DC and the ACSR R-DC alloys. Compared to the T-DC alloy, the ultimate tensile strength, elongation and yield strength of the ACSR + UV R-DC alloy were increased by 34%, 122% and 19%, respectively. This was because the ACSR + UV R-DC technique gave the alloy the characteristics of high density, fine spherical α1-Al grain and a fine and uniform β-phase, which improved the fracture behaviour of the alloy. The thermal conductivity of the ACSR + UV R-DC alloy was 184 W/(m K), which was 10.2% and 3.4% higher than that of T-DC and ACSR R-DC alloys, respectively. This was because the refined eutectic silicon and β phases in the ACSR + UV R-DC alloy facilitated an easier electron flow through the eutectic region, and the decrease in porosity increased the effective area of heat conduction.

Microstructure Evolution and Mechanical Properties of Rheo-Processed ADC12 Alloy

Primary phase evolution of rheo-processed ADC12 aluminum alloy

Rheo-Processing of Near-Eutectic Adc12 Alloy

Effect of Alloying Elements and Processing Parameters on Microstructure and Properties of 1XXX Aluminium Alloys

Microstructure and mechanical properties of rheo-diecasted A390 alloy

Microstructural Evolution and Mechanical Properties of Rapidly Solidified Ni-Ge Alloys

Microstructure and Mechanical Properties of Rheo-Diecast Hypereutectic Al–Si Alloy with 2%fe Assisted with Ultrasonic Vibration Process

Influence of Rheo-Diecasting Processing Parameters on Microstructure and Mechanical Properties of Hypereutectic Al–30%Si Alloy

Microstructure and Properties of ADC12 Aluminum Alloy Improved by Casting-forging Combined Forming

Microstructure Evolution and Mechanical Properties of Rheo-Squeeze Casting AZ91-Ca Alloy During Heat Treatment

Microstructure and Mechanical Properties of a Rapidly-Solidified and Extruded Al-13.2Zn-2.5Mg −1.2Cu-0.2Zr Alloy and Its Aging Hardening Response at 120 °C

Towards high performance Al–Si–Fe alloy castings via rheo-diecasting: Effect of injection velocity and heat treatment on microstructure evolution and property

Research on Microstructure and Mechanical Properties of Rheological Die Forging Parts of Al-6.54Zn-2.40Cu-2.35Mg-0.10Zr(-Sc) Alloy

Microstructure, Precipitates Behavior, and Mechanical Properties of Age-Hardened Al-Mg-Si Alloy Sheet Fabricated by Twin-Roll Casting

Microstructure Evolution and High-Temperature Performances of AA6111 Alloy Strengthened by Sc, Zr Co-Microalloying

Enhanced comprehensive performance via alloying and rheo-diecasting in a semi-solid Al–Si–Fe–Mg–Cu–Sr alloy

Evolution of Microstructure and Mechanical Properties of the Rheo-Diecast Mg-12Gd-3Y-1Zn-0.4Zr Alloy during Heat Treatment

Microstructure and Properties of Rheo-Diecast Al-20Si-2Cu-1Ni-0.4Mg Alloy with Direct Ultrasonic Vibration Process

Effects of rare earth Er additions on microstructure development and mechanical properties of die-cast ADC12 aluminum alloy

Synchronously Improving the Thermal Conductivity and Mechanical Properties of Al–Si–Fe–Mg–Cu–Zn Alloy Die Castings Through Ultrasonic-Assisted Rheoforming

Microstructural Evolution and Mechanical Properties of 2195 Al-Li Alloy Processed by Rapid Solidification and Thermo-Mechanical Processing