Abstract:An ultrasonic vibration-assisted air-cooled stirring rod process (ACSR + UV) was used to efficiently prepare a large-volume semisolid slurry with a mass of more than 40 kg. A low-cost Al–Si–Fe–Mg–Cu–Zn die-casted alloy with high thermal conductivity, high plasticity and medium strength was developed. The alloy was used to manufacture large, thin-walled parts for 5G base stations by using the ACSR + UV rheological die-casting (ACSR + UV R-DC) process. Investigations were performed on the microstructure, porosity, mechanical properties, fracture behaviour and thermal conductivity of the ACSR + UV R-DC alloy, which was then compared to traditionally die-casted (T-DC) and ACSR R-DC alloys. The mechanisms for the microstructural refinement and enhancement of the mechanical and thermal conductivity performances of the ACSR + UV R-DC alloy were also analysed. The results showed that the ACSR + UV process increased the nucleation rate of the melt due to the increase in the nucleation area and the generation of cavitation bubbles. A radial- and an axial-forced convection was also generated inside the melt under the combined effects of acoustic flow and mechanical stirring, thereby homogenising the melt composition field and the temperature field. Therefore, the ACSR + UV R-DC process not only refined the primary α-Al (α1-Al), the eutectic silicon and the secondary α-Al (α2-Al), but also greatly improved the morphology and the distribution of the β-Al5FeSi phase. The mechanical properties of the ACSR + UV R-DC alloy were higher than those of the T-DC and the ACSR R-DC alloys. Compared to the T-DC alloy, the ultimate tensile strength, elongation and yield strength of the ACSR + UV R-DC alloy were increased by 34%, 122% and 19%, respectively. This was because the ACSR + UV R-DC technique gave the alloy the characteristics of high density, fine spherical α1-Al grain and a fine and uniform β-phase, which improved the fracture behaviour of the alloy. The thermal conductivity of the ACSR + UV R-DC alloy was 184 W/(m K), which was 10.2% and 3.4% higher than that of T-DC and ACSR R-DC alloys, respectively. This was because the refined eutectic silicon and β phases in the ACSR + UV R-DC alloy facilitated an easier electron flow through the eutectic region, and the decrease in porosity increased the effective area of heat conduction.

Rheo-Diecasting of Magnesium Alloys

Microstructures refinement and mechanical properties enhancement of aluminum and magnesium alloys by combining distributary-confluence channel process for semisolid slurry preparation with high pressure die-casting

Towards high performance Al–Si–Fe alloy castings via rheo-diecasting: Effect of injection velocity and heat treatment on microstructure evolution and property

Study on Semisolid Rheo-Diecasting Process, Microstructure and Mechanical Properties of Mg-6Al-1Ca-0.5Sb Alloy with High Solid Fraction

Microstructure and Mechanical Properties of Rheo-Diecast Hypereutectic Al–Si Alloy with 2%fe Assisted with Ultrasonic Vibration Process

Semi-solid Rheo-Diecast Mg-xGd-3Y-1Zn-0.4Zr (wt.%) Alloys and Their Comparison with Conventional HPDC Alloys

Study on a Semi-Solid Rheo-Diecasting Process With AZ91D Alloy Slurry

Semisolid rheoforming of magnesium alloys: A review

Rheo-Forming AZ91D Magnesium Alloy Using Enthalpy Equilibrium Electromagnetic-Stirring Process

New technique for preparing A356 alloy semisolid slurry and its rheo-diecast microstructure and properties

Rheo-Processing of Near-Eutectic Adc12 Alloy

A novel rheological high pressure die-casting process for preparing large thin-walled Al–Si–Fe–Mg–Sr alloy with high heat conductivity, high plasticity and medium strength

Industrialization of Aluminum Alloy Uniform Solidification Controlled Rheological Die Casting

Microstructure and Mechanical Properties of Magnesium Alloy AZ91D Produced by Rheo-Diecasting Process

Producing Structural High Integrity Castings with Minimum Carbon Footprint with the Comptech-Rheocasting Process

Rheoforming Processing of Al Alloys with Slurry Preparation System and Component Shaping System Apart

Solidification behavior and enhanced properties of semi-solid Al–8Si–0.5Fe alloys fabricated by rheo-diecasting

Synchronously Improving the Thermal Conductivity and Mechanical Properties of Al–Si–Fe–Mg–Cu–Zn Alloy Die Castings Through Ultrasonic-Assisted Rheoforming

Microstructure and mechanical properties of Mg-Gd-Y-Zn-Zr alloy prepared by rheo-diecasting

Recycling of High Grade Die Casting Am Series Magnesium Scrap with the Melt Conditioned High Pressure Die Casting (Mc-Hpdc) Process