Fabrication of Carbon Nanotube Reinforced Al Composites with Well-Balanced Strength and Ductility

Xudong Yang,Enzuo Liu,Chunsheng Shi,Chunnian He,Jiajun Li,Naiqin Zhao,Katsuyoshi Kondoh
DOI: https://doi.org/10.1016/j.jallcom.2013.02.066
IF: 6.2
2013-01-01
Journal of Alloys and Compounds
Abstract:An approach was developed to fabricate carbon nanotube (CNT)-reinforced Al composites. In a typical process, the Co catalyst was evenly deposited on the surface of Al powder by impregnation route, and then the CNTs were grown in the Al powder by chemical vapor deposition to obtain CNT/Al powders. After ball-milling of the obtained powders for a short time, the CNT/Al composites were fabricated by compacting, sintering and hot extrusion of the ball-milled powders. During this process, the well dispersed CNT reinforcement is deeply embedded in the Al powder forming an effective interface bonding with matrix. As a result, the CNT/Al composites containing 2.5 wt.% CNTs exhibit the ultimate tensile strength of 334 MPa which is 1.7 times higher than that of unreinforced Al, and good ductility of similar to 18% elongation to failure. Thus, well-balanced strength and ductility are achieved in CNT-reinforced Al composites. (C) 2013 Elsevier B.V. All rights reserved.
What problem does this paper attempt to address?