Abstract:The samples of commercial pure copper bars were severely plastic-deformed by different pretension and subsequently by different turns of torsion. Microstructure evolution of deformed samples was characterized using optical microscopy (OM). Longitudinal observations showed the formation of gradient microstructure with the maximum grain refinement in the surface layer of bars. Microindentation tests were conducted in the indenter load range of 100–450mN and at a loading rate of 9.6841mN/s. The hardness and Young's modulus were analyzed in the transversal section of samples using the method of Oliver and Pharr. Based on the strain gradient plasticity theory, the densities of statistically stored dislocations (SSDs) and geometrically necessary dislocations (GNDs) were calculated according to the Taylor dislocation model, respectively. Experimental results reveal that the hardness and Young's modulus decrease with the indenter load increasing. Indentation size effect on the hardness is relatively more significant than the counterpart of Young's modulus. In a certain pretension condition, the hardness values increase fast and subsequently slowly with the increase of applied torsion turns. The torsion process seems to effectively increase the material hardening due to the introduced simple shear strain. Compared to the hardness analysis, Young's modulus gently increases with the increase of torsion turns. That is due to the saturation of mechanical damage and/or crack introduced by severe deformation. In the combined tension–torsion loading, both densities of GNDs and SSDs increase with the increase of torsion turns. However, the SSDs density is higher than that of GNDs in spite of the same order magnitude. The torsional shear strain enhances the non-uniform deformation and stimulates the propagation of GNDs.

Experimental Microindentation of Pure Copper Subjected to Severe Plastic Deformation by Combined Tension–torsion

Effect of cryogenic impact deformation and subsequent annealing on microstructure and microhardness of pure copper

Microstructure evolution, hardening and thermal behavior of commercially pure copper subjected to torsion deformation

Micro-structural Evolution Subjected to Combined Tension–torsion Deformation for Pure Copper

Experimental Study on Pure Copper Subjected to Different Severe Plastic Deformation Modes

The Meso-inhomogeneous Deformation of Pure Copper under Tension–Compression Cyclic Strain Loading

Microstructural Evolution and Micro‐Compression in High‐Purity Copper Processed by High‐Pressure Torsion

Influence of Deformation Stress Triaxiality on Microstructure and Microhardness of Pure Copper Processed by Simultaneous Torsion and Tension

Electron Backscatter Diffraction Analysis of the Microstructure Fineness in Pure Copper under Torsional Deformation

Effects of Torsional Deformation on the Mechanical Properties and Microstructures of a Commercial Pure Copper

Numerical and Experimental Studies of Pure Copper Processed by a New Severe Plastic Deformation Method

Anisotropy of Yielding/Hardening and Micro-Inhomogeneity of Deforming/Rotating for A Polycrystalline Metal under Cyclic Tension Compression

Influence of Pre-Tension on Free-End Torsion Behavior and Mechanical Properties of an Extruded Magnesium Alloy.

Microstructures and Mechanical Properties of Commercial Hot‐Extruded Copper Processed by Torsion Deformation

Microstructural Changes Produced by Fatigue in High-Purity Copper Severely Deformed by Cryogenic Rolling

The Effect of Reverse Strain on Microstructure and Strengthening of Copper Fabricated by Severe Plastic Deformation of Torsion Process

Numerical and Experimental Studies of Deep Indentation on Single Crystals

Investigations of Micro-Deformation in Monocrystalline Copper at Low Temperatures via Indentation

Ultrafine-grained Pure Copper Fabricated by Severe Plastic Deformation of Combined Tensile and Torsion

Microstructure and Texture of Pure Copper under Large Compression Deformation and Different Annealing Times

Nanoindentation Response of Monocrystalline Copper under Various Tensile Pre-Deformations Via Molecular Dynamic Simulations