Synthesis and Magnetic Properties of Monodisperse CoFe2O4 Nanoparticles Coated by SiO2
Dengwei Hu,Fan Zhao,Zhen Zhang,Lei Miao,Rong Ma,Weixing Zhao,Lijun Ren,Gaini Zhang,Le Zhai,Dongmei Wang,Shumei Dou
DOI: https://doi.org/10.1016/j.ceramint.2018.09.014
IF: 5.532
2018-01-01
Ceramics International
Abstract:The monodisperse CoFe2O4 nanoparticles were synthesized by a modified chemical coprecipitation method. Coating SiO2 on the surface of the CoFe2O4 nanoparticles was carried out to keep single domain particles non-interacting with cubic magnetocrystalline anisotropy. The Curie temperatures (T-c) of the monodisperse CoFe2O4 nanoparticles can be accurately measured because the SiO2 shells prevented the aggregation and growth of nanoparticles at high temperature. The magnetic properties of the CoFe2O4@SiO2 nanoparticles with core-shell structure in a wide temperature range (300 similar to 950 K) were investigated. It is remarkable that the coercive field (H-c) of CoFe2O4 nanoparticles increased from about 760 Oe to 1806 Oe after being coated with SiO2, which increased by 137.6% compared to the uncoated samples at 300 K. The saturation magnetization (M-s) of the CoFe2O4@SiO2 nanoparticles is 34.59 emu/g, which is about 52% of the naked CoFe2O4 nanoparticles value (66.51 emu/g) at 300 K. The hysteresis loops of the CoFe2O4@SiO2 nanoparticles showed an orderly magnetic behavior at high temperature, such as the M-s, remanence magnetization (M-r) and H-c decreased as temperature increasing, being equal to zero near T-c. This is a good indication that the CoFe2O4@SiO2 nanoparticles are suitable for a wide variety of technological applications at high temperature.