Abstract:Abstract In the present study, CoFe 2 O 4 and CoFe 2-x Gd x O 4 nanoparticles were synthesized by the hydrothermal process. The CoFe 2 O 4 nanoparticles were synthesized at different temperatures (70 o C, 100 o C, 150 o C, and 200 o C), molar ratio of CoCl 2 / FeCl 3 ( 0 / 2 , 0 . 75 / 2, 1 / 2, 1 . 5/2, and 2 / 2). Gadolinium-doped cobalt ferrite (CoFe 2-x Gd x O 4 ) nanoparticles have also been synthesized with Gd/Fe molar ratios of 0.18 and 0.53. The XRD patterns indicate that cobalt ferrite and Gadolinium-doped cobalt ferrite nanoparticles have been successfully synthesized without impurities with a medium degree of crystallinity. The XRD patterns show that by increasing the synthesis temperature from 70 o C to 200 o C, the size of the nanoparticles decreased from 50.49nm to 32.45nm while the morphology of the nanoparticles also changed from a shapeless and agglomerated state to a spherical shape. The XPS curve illustrated several peaks corresponding to Fe +3 , Co +2 , and O 1s. The binding energies for Co and Fe were consistent with Fe 2p and Co 2p binding energies for cobalt ferrite nanoparticles. The magnetic saturation value (M s ) increased from 17.253 emu/g to 54.438 emu/g with a rise in the synthesis temperature. The effects of FeCl 3 / CoCl 2 molar ratio on the magnetic properties showed the highest value of M s (54.438 emu/g) and the coercivity (H C ) of 744.56 Oe for a 2/1 molar ratio. The addition of gadolinium to the composition resulted in a reducing of the magnetic properties of nanoparticles; accordingly, the amount of saturated magnetization was reduced to 22.469 emu/g. Another effect of gadolinium dopant in the composition was a change in nanoparticle morphology from spherical to rod shape. The final aim of this study was to investigate the possible utilization of CoFe 2 O 4 and CoFe 2-x Gd x O 4 nanoparticles in medical treatment in the near future.

Synthesis and Magnetic Properties of CoFe<sub>2</sub>O<sub>4</sub> Nano-Particles

CoFe_2O_4 Nanoparticles Synthesized by Hydro-Thermal Method and Its Magnetic Properties

HYDROTHERMAL SYNTHESIS AND MAGNETIC PROPERTIES OF CoFe2O4 NANO-POWDER

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Synthesis of CoFe<sub>2</sub>O<sub>4</sub> nanoparticles with tunable magnetism by the modified hydrothermal method

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Hydrothermal Synthesis and Properties of CoFe2O4 Magnetic Nanoparticles

The Synthesis and Thermal Effect of CoFe2O4 Nanoparticles

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Synthesis and Characterization of Nano-sized Cobalt Ferrite Powders with High Specific Area and Magnetic Properties in Template-assisted Sol-gel Method

Synthesis and magnetic properties of CoFe2O4 ferrite nanoparticles

Chemical Synthesis and Magnetic Study of Nanocrystalline Thin Films of Cobalt Spinel Ferrites

Synthesis Factors Dependence of Magnetic Properties of CoFe2O4 and CoFe2-xGdxO4 Semicrystalline Nanoparticles with desired Morphology through Hydrothermal Procedure

Synthesis of CoFe 2 O 4 nanoparticles with tunable magnetism by the modified hydrothermal method

Synthesis and Magnetic Properties of Cofe2o4 and Mnfe2o4 Nano Composites

Magnetic Properties for the Single-Domain CoFe2O4 Nanoparticles Synthesized by the Hydrothermal Method

Synthesis and Size-Selective Precipitation of Monodisperse Nonstoichiometric MxFe3–xO4 (M = Mn, Co) Nanocrystals and Their DC and AC Magnetic Properties

Study on Supercritical Hydrothermal Synthesis of CoFe2O4 Nanoparticles

Sdudy of Magnetic Properties and Synthesis of Co_(0.2)Fe_(2.8)O_4 Porous Microspheres

Synthesis and Magnetic Properties of CoFe&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;4&lt;/sub&gt; Nano-Particles