Abstract:The structural evolution and magnetic properties of nanostructured copper ferrite, CuFe2O4, have been investigated by x-ray diffraction, Mossbauer spectroscopy, and magnetization measurements. Nanometre-sized CuFe2O4 particles with a partially inverted spinel structure were synthesized by high-energy ball milling in an open container with grain sizes ranging from 9 to 61 nm. Superparamagnetic relaxation effects have been observed in milled samples at room temperature by Mossbauer and magnetization measurements. At 15 K, the average hyperfine held of CuFe2O4 decreases with decreasing average grain size while the coercive force, shift of the hysteresis loop, magnetic hardness, and saturation magnetization at 4.2 K increase with decreasing average grain size. At 295 K the coercive-held dependence on the average grain size is described, with particles showing superparamagnetic relaxation effects. At 4.2 K the relationship between the coercive field and average grain size can be attributed to the change of the effective anisotropy constant of the particles. The interface anisotropy of nanostructured CuFe2O4 is found to be about 1.8(1) x 10(5) erg cm(-3). Although spin canting was present, approximately 20% enhancement of the saturation magnetization in CuFe2O4 nanoparticles was observed, which could be explained by a cation redistribution induced by milling. The high-held magnetization irreversibility and shift of the hysteresis loop detected in our samples have been assigned to a spin-disordered phase, which has a spin-freezing temperature of approximately 50 K.

Understanding the Formation of Ultrafine Spinel CoFe2O4 Nanoplatelets and Their Magnetic Properties

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Tuning the Formation and Functionalities of Ultrafine CoFe2O4 Nanocrystals Via Interfacial Coherent Strain

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Synthesis and Magnetic Properties of CoFe<sub>2</sub>O<sub>4</sub> Nano-Particles

Effect of Zn Substitution on Morphology and Magnetic Properties of Cufe2o4 Nanofibers

CoFe_2O_4 Nanoparticles Synthesized by Hydro-Thermal Method and Its Magnetic Properties

Magnetic properties of different CoFe2O4 nanostructures: nanofibers versus nanoparticles

CoFe2O4 nanopowder synthesis by a solid-liquid cation-exchange process and their magnetic properties

Magnetic Properties of Nanostructured Cufe2o4

Preparation and Magnetic Properties of Cobalt-Doped FeMn2O4 Spinel Nanoparticles

Chemical Synthesis and Magnetic Study of Nanocrystalline Thin Films of Cobalt Spinel Ferrites

Microstructure, Growth Mechanism, Magnetoelectricity, and Raman Scattering of Featherlike CoFe2O4–BaTiO3 Nanostructures

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Enhanced Magnetization in CoFe2O4 Through Hydrogen Doping

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Sub-20 nm-Fe3O4 square and circular nanoplates: synthesis and facet-dependent magnetic and electrochemical properties.

Synthesis and magnetic properties of CoFe2O4 ferrite nanoparticles

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

{110} Plane Orientation Driven Superior Li-ion Battery Performance and Room Temperature Ferromagnetism in Co3O4 Nanostructures

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles