Abstract:Cobalt ferrite (CoFe2O4) nanoparticles were synthesized by using the hydrothermal route with the addition of trisodium citrate dihydrate (Na(3)CA center dot 2H(2)O). The formation of CoFe2O4 nanoparticles with size ranging from 13 to 19 nm was confirmed by X-ray diffraction, energy dispersive X-ray analysis, and Fourier transform infrared spectroscopy; the clear-cut sharp of the nanoparticles was observed by transmission electron microscopy. By these characterization methods, the evolution of lattice constant and morphologies of the nanoparticles with the addition of Na(3)CA center dot 2H(2)O is observed. Furthermore, the magnetic hysteresis loops measured at room temperature indicate that the magnetic properties of the products also show clear relationship with the masses of Na(3)CA center dot 2H(2)O. For example, coercivity and high-field paramagnetic susceptibility increase with the increasing masses of Na(3)CA center dot 2H(2)O, whereas the saturation magnetization and the effective magnetic anisotropy constant have the maximum values as the mass of Na(3)CA center dot 2H(2)O is 1 g. This change of magnetic properties is related with the expanded lattice and the varied size and shape because of the addition of Na(3)CA center dot 2H(2)O.

Simplified Synthesis of Single-Crystalline Magnetic CoFe2O4 Nanorods by a Surfactant-Assisted Hydrothermal Process

Synthesis of CoFe<sub>2</sub>O<sub>4</sub> nanoparticles with tunable magnetism by the modified hydrothermal method

Synthesis and Characterization of Single-Crystalline Mnfe(2)O(4) Nanorods Via A Surfactant-Free Hydrothermal Route

Synthesis of CoFe 2 O 4 nanoparticles with tunable magnetism by the modified hydrothermal method

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Cobalt Ferrite Nanorods Synthesized with a Facile “Green” Method in a Magnetic Field

Ultrasonic-assisted Surfactant-Free Synthesis of Highly Magnetized FeCo Alloy Nanocrystallite from Ferric and Cobalt Salt

Hydrothermal Synthesis of Magnetic Fe_3O_4 Hexagonal and Single Crystal Nanorods

Hydrothermal Synthesis of Magnetic Fe3O4 Hexagonal and Single Crystal Nanorods

A Soft-Template-Assisted Hydrothermal Approach to Single-Crystal Fe3o4 Nanorods

Room Temperature Synthesis of Rod-Like FeC{sub 2}o{sub 4}{center_dot}2h{sub 2}O and Its Transition to Maghemite, Magnetite and Hematite Nanorods Through Controlled Thermal Decomposition

Chemical Synthesis, Structure and Magnetic Properties of Co Nanorods Decorated with Fe3O4 Nanoparticles

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Surfactant-assisted synthesis of alpha-Fe2O3 nanotubes and nanorods with shape-dependent magnetic properties.

Surfactant-Assisted Synthesis of α-Fe<sub>2</sub>O<sub>3</sub>Nanotubes and Nanorods with Shape-Dependent Magnetic Properties

Solution-phase Synthesis of Single-Crystalline Fe3O4 Magnetic Nanobelts

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Unique Magnetic Properties and Magnetization Reversal Process of CoFe2O4 Nanotubes Fabricated by Electrospinning

Synthesis of ferromagnetic single-crystalline cobalt nanobelts via a surfactant-assisted hydrothermal reduction process

Synthesis and Magnetic Properties of Single‐Crystals of MnFe2O4 Nanorods

Convenient synthesis of single crystalline magnetic Fe3O4 nanorods