Abstract:Fe80-xCo20Bx (x = 12-15 at%) alloy ribbons consisting of single bcc phase (12%B), amorphous plus bcc-Fe(Co) mixed phases (13%B) and amorphous single phase (14%B and 15%B) were synthesized by the melt-spinning technique. It is noticed that all the alloy ribbons containing amorphous phase exhibit good bending ductility in the as-spun state and even after annealing which leads to the precipitation of nanoscale bcc-Fe(Co) phase. The amorphous plus bcc-Fe(Co) phase alloys with lower hardness exhibited a number of microcracks in the region near the hardness indentation trace, in addition to distinct slip step markings. The decrease in hardness and the maintenance of ductility in the nanocrystalline state are interpreted to originate from microcrack-induced softening phenomenon. The nanocrystalline alloys also exhibit good soft magnetic properties with high saturation magnetization above 1.7 T in combination with low coercivity of about 20 A/m. The good bending ductility as well as the microcrack-induced softening for the amorphous alloys including nanoscale bcc-Fe(Co) phase is believed to be the first evidence in the long development history of Fe-based nanocrystalline soft magnetic alloys. The finding of the ductile Fe-based nanocrystalline alloys with high saturation magnetization is encouraging for further extension of nanocrystalline magnetic materials. (C) 2015 Elsevier B.V. All rights reserved.

Ultrasonic-assisted Surfactant-Free Synthesis of Highly Magnetized FeCo Alloy Nanocrystallite from Ferric and Cobalt Salt

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Nanocomposites of iron-cobalt alloy and magnetite: Controllable solvothermal synthesis and their magnetic properties

Positive Microemulsion Synthesis and Magnetic Property of Amorphous Multicomponent Co-, Ni- and Cu-based Alloy Nanoparticles

Crystallization kinetics and magnetic properties of Fe 63.5Co10Si13.5B9Cu 1Nb3 nanocrystalline powder cores

Sonochemical synthesis, structural and magnetic properties of air-stable Fe/Co alloy nanoparticles

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Synthesis of CoFe<sub>2</sub>O<sub>4</sub> nanoparticles with tunable magnetism by the modified hydrothermal method

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

Simplified Synthesis of Single-Crystalline Magnetic CoFe2O4 Nanorods by a Surfactant-Assisted Hydrothermal Process

Large-Scale Controlled Synthesis of FeCo Nanocubes and Microcages by Wet Chemistry

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles

Softening and Good Ductility for Nanocrystal-Dispersed Amorphous Fe–Co–B Alloys with High Saturation Magnetization above 1.7 T

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Synthesis and Magnetic Properties of FeCo Alloy Nanoparticles by Hydrogen Plasma Metal Reaction

Structure and Magnetic Properties of FeCo–SiO2 Nanocomposite Synthesized by a Novel Wet Chemical Method

Synthesis of CoFe 2 O 4 nanoparticles with tunable magnetism by the modified hydrothermal method

Facile Route to Preparation of Fe-Co Microclusters with Highly Enhanced Magnetic Performances

FeCo-based Amorphous Alloys with High Ferromagnetic Elements and Large Annealing Processing Window

Microstructure and Soft-Magnetic Properties of FeCoPCCu Nanocrystalline Alloys

One-pot synthesis and magnetic properties of hollow Fe<sub>70</sub>Co<sub>30</sub> nanospheres