Abstract:The monodisperse CoFe2O4 nanoparticles were synthesized by a modified chemical coprecipitation method. Coating SiO2 on the surface of the CoFe2O4 nanoparticles was carried out to keep single domain particles non-interacting with cubic magnetocrystalline anisotropy. The Curie temperatures (T-c) of the monodisperse CoFe2O4 nanoparticles can be accurately measured because the SiO2 shells prevented the aggregation and growth of nanoparticles at high temperature. The magnetic properties of the CoFe2O4@SiO2 nanoparticles with core-shell structure in a wide temperature range (300 similar to 950 K) were investigated. It is remarkable that the coercive field (H-c) of CoFe2O4 nanoparticles increased from about 760 Oe to 1806 Oe after being coated with SiO2, which increased by 137.6% compared to the uncoated samples at 300 K. The saturation magnetization (M-s) of the CoFe2O4@SiO2 nanoparticles is 34.59 emu/g, which is about 52% of the naked CoFe2O4 nanoparticles value (66.51 emu/g) at 300 K. The hysteresis loops of the CoFe2O4@SiO2 nanoparticles showed an orderly magnetic behavior at high temperature, such as the M-s, remanence magnetization (M-r) and H-c decreased as temperature increasing, being equal to zero near T-c. This is a good indication that the CoFe2O4@SiO2 nanoparticles are suitable for a wide variety of technological applications at high temperature.

Synthesis, Structure and Magnetic Properties of CoFe2O4 Ferrite Nanoparticles

Synthesis and magnetic properties of CoFe2O4 ferrite nanoparticles

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Synthesis of CoFe<sub>2</sub>O<sub>4</sub> nanoparticles with tunable magnetism by the modified hydrothermal method

HYDROTHERMAL SYNTHESIS AND MAGNETIC PROPERTIES OF CoFe2O4 NANO-POWDER

Synthesis and Characterization of CoFe 2 O 4 Nanoparticles

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

CoFe_2O_4 Nanoparticles Synthesized by Hydro-Thermal Method and Its Magnetic Properties

Synthesis and characterization of CoFe2O4 ferrite nanoparticles obtained by an electrochemical method

Synthesis of CoFe 2 O 4 nanoparticles with tunable magnetism by the modified hydrothermal method

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles

SYNTHESIS OF CoFe2O4 NANOPARTICLES BY COPRECIPITATION METHOD AND ITS MAGNETIC PROPERTIES

Microstructure and Magnetic Properties of Nanosized CoFe_2O_4 Particles

Synthesis and Magnetic Properties of Monodisperse CoFe2O4 Nanoparticles Coated by SiO2

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Magnetic properties of CoFe2O4 ferrite doped with rare earth ion

Characterization and magnetic properties of CoFe2O4 nanoparticles synthesized by the co‐precipitation method

Composition And Magnetic Properties Of Cobalt Ferrite Nano-Particles Prepared By The Co-Precipitation Method

Synthesis and Magnetic Properties of CoFe2/CoFe2O4 Nanoparticles Diluted in the MgO Matrix