Abstract:Cobalt carbides (Co2C and Co3C) nanocomposites exhibit interesting hard magnetic property, controlled synthesis of individual phase facilitates to clarify the magnetism of each, but it is difficult to obtain the single phase. We present a new approach to address this issue via a polyol refluxing process, using cobalt laurate as the precursor. The single phase Co2C magnetic nanochains self-assembled by nanoparticles are synthesized. The precursor is the key factor for controlling the growth kinetics of the Co2C nanochains. Cobalt, instead of cobalt carbides, is produced if cobalt chloride, acetate and acetylacetonate replace cobalt laurate as the precursor, respectively. The evolution of the growth process has been studied. In the formation of Co2C, first fcc-Co produces, then it transforms into Co2C by carbon diffusion process, and the produced carbon first exists in disordered state and then a small amount of them transforms into graphite. Saturation magnetization (Ms) of Co2C nanochains obtained at 300 degrees C for 20, 60, and 180 min are 27.1, 18.9, and 10.9 emu g(-1), respectively. The decrease of Ms caused by increasing carbon content, and the carbon content are much larger than the stoichiometric ratio value of Co2C (9.2 wt%). The Co2C nanochains have mesoporous pore of 3.8 nm and the specific surface area of 48.6 m(2) g(-1). (C) 2018 Elsevier B.V. All rights reserved.

Synthesis of ferromagnetic single-crystalline cobalt nanobelts via a surfactant-assisted hydrothermal reduction process

A Hydrothermal Reduction Route to Single‐Crystalline Hexagonal Cobalt Nanowires

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

Hydrothermal Synthesis Of Cobalt-Basic-Carbonate Nanobelts

Shape-controlled Synthesis and Self-Assembly of Hexagonal Cobalt Ultrathin Nanoflakes

Solvothermal synthesis of single-crystalline hexagonal cobalt nanofibers with high coercivity

Formation of Cobalt Hollow Nanospheres Via Surfactant-Assisted Hydrothermal Progress

Effect of Size Distribution on Magnetic Properties in Cobalt Nanowires

Self-Assembled Two-Dimensional Structure of Magnetic Cobalt Nanocrystals

Solvothermal Synthesis of NiCo Alloy Icosahedral Nanocrystals

Selective-precursor reducing route to cobalt nanocrystals and ferromagnetic property

A Magnetic-Field-Assisted Solution-Phase Route To Cobalt Thin Film Composed Of Cobalt Nanosheets

Synthesis of Cobalt Nanocrystals by High Temperature Solution Phase Reducing Method and Their Two-dimensional Ordered Superlattices

Simplified Synthesis of Single-Crystalline Magnetic CoFe2O4 Nanorods by a Surfactant-Assisted Hydrothermal Process

Controlled Synthesis of Cobalt Flowerlike Architectures by A Facile Hydrothermal Route

Synthesis of Cobalt Nanowires in Aqueous Solution under an External Magnetic Field

Controlled Synthesis of Co2C Nanochains Using Cobalt Laurate As Precursor: Structure, Growth Mechanism and Magnetic Properties

Synthesis of Co submicrospheres self-assembled by Co nanosheets via a complexant-assisted hydrothermal approach

Synthesis and Characterization of Structure Controlled Nano-cobalt Particles

Synthesis and characterization of ferromagnetic cobalt nanospheres, nanodiscs and nanocubes

Superstructures of Self-Assembled Cobalt Nanocrystals