Abstract:Magnetic metallic cobalt with different hierarchical structures, such as dendritic particles, flowery particles, and flocky spheres, has been successfully prepared by using a simple solvothermal process in which the relative amounts of H2C2O4 and N2H4 center dot H2O in the reaction system were rationally adjusted. The Co crystals with hierarchical structure had a hexagonal-close-packed (hcp) structure. The dendritic Co crystal comprises several 1-5 mu m long dendrites, and the hierarchical assemblies radiate from the center. The flower-like Co submicrocrystals are composed of petal-like crystals around 1.5 mu m in diameter and 100-200 nm thick. Interestingly, an intergrade from single-crystal to polycrystalline structures for flowerlike Co submicrocrystals is observed. The flocky spheres, about 600 nm in diameter, consist of 5 nm thick nanosheets. In addition, a growth mechanism is proposed which is based on the evolution of the structure and morphology with increasing reaction time. Further magnetic measurements for the Co crystals with different hierarchical structures indicated that the morphology of the Co crystals had an obvious influence on their magnetic properties.

Self-Assembled Two-Dimensional Structure of Magnetic Cobalt Nanocrystals

Synthesis of Cobalt Nanocrystals by High Temperature Solution Phase Reducing Method and Their Two-dimensional Ordered Superlattices

Hydrothermal Microemulsion Synthesis of Cobalt Nanorods and Self-Assembly into Square-Shaped Nanostructures

Synthesis of ferromagnetic single-crystalline cobalt nanobelts via a surfactant-assisted hydrothermal reduction process

Shape-controlled Synthesis and Self-Assembly of Hexagonal Cobalt Ultrathin Nanoflakes

Nanostructures of Ni and NiCo Amorphous Alloys Synthesized by a Double Composite Template Approach

Ordered Arrays and Magnetic Properties of Cobalt Nanoparticles

Solvothermal Synthesis of NiCo Alloy Icosahedral Nanocrystals

Controlled synthesis and anomalous magnetic properties of relatively monodisperse CoO nanocrystals.

A Hydrothermal Reduction Route to Single‐Crystalline Hexagonal Cobalt Nanowires

The Dependence of Co Nanoparticle Sizes on the Ratio of Surfactants and the Influence of Different Crystal Sizes on Magnetic Properties

Synthesis and Characterization of Structure Controlled Nano-cobalt Particles

Synthesis and Characterization of Metallic Co with Different Hierarchical Structures Prepared by A Simple Solvothermal Method

Synthesis and Magnetic Properties of Chain-like Cobalt Assemblies

Cobalt–iron cyanide hollow cubes: Three-dimensional self-assembly and magnetic properties

Assembly of non-crystalline cobalt particles into crystalline tricobalt tetroxide nanowires under an external magnetic field

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

Controlled Synthesis of Cobalt Flowerlike Architectures by A Facile Hydrothermal Route

Synthesis of Co submicrospheres self-assembled by Co nanosheets via a complexant-assisted hydrothermal approach

Organic Colloid Method to Prepare Ultrafine Cobalt Nanoparticles with the Size of 2 Nm

Metallic Cobalt Microcrystals with Flowerlike Architectures: Synthesis, Growth Mechanism and Magnetic Properties