Abstract:Magnetic metallic cobalt with different hierarchical structures, such as dendritic particles, flowery particles, and flocky spheres, has been successfully prepared by using a simple solvothermal process in which the relative amounts of H2C2O4 and N2H4 center dot H2O in the reaction system were rationally adjusted. The Co crystals with hierarchical structure had a hexagonal-close-packed (hcp) structure. The dendritic Co crystal comprises several 1-5 mu m long dendrites, and the hierarchical assemblies radiate from the center. The flower-like Co submicrocrystals are composed of petal-like crystals around 1.5 mu m in diameter and 100-200 nm thick. Interestingly, an intergrade from single-crystal to polycrystalline structures for flowerlike Co submicrocrystals is observed. The flocky spheres, about 600 nm in diameter, consist of 5 nm thick nanosheets. In addition, a growth mechanism is proposed which is based on the evolution of the structure and morphology with increasing reaction time. Further magnetic measurements for the Co crystals with different hierarchical structures indicated that the morphology of the Co crystals had an obvious influence on their magnetic properties.

Growth of Dendritic Cobalt Nanocrystals at Room Temperature

Room Temperature Self-Assembly Growth of Cobalt Nanowires under Magnetic Fields

Liquid Phase Preparations and Performances of Magnetic Dendritic Nanocrystalline Co

A Hydrothermal Reduction Route to Single‐Crystalline Hexagonal Cobalt Nanowires

Manipulation of Morphology and Magnetic Properties in Cobalt Nanowires

Synthesis of ferromagnetic single-crystalline cobalt nanobelts via a surfactant-assisted hydrothermal reduction process

Selective-precursor reducing route to cobalt nanocrystals and ferromagnetic property

Solvothermal Synthesis of NiCo Alloy Icosahedral Nanocrystals

Controlled Synthesis of Rice Ear-Like Cobalt Microcrystals at Room Temperature

Structure and magnetic properties of hierarchical cobalt dendrites

Versatile fabrication of dendritic cobalt microstructures using CTAB in high alkali media

Synthesis of Cobalt Nanocrystals by High Temperature Solution Phase Reducing Method and Their Two-dimensional Ordered Superlattices

Solvothermal synthesis of single-crystalline hexagonal cobalt nanofibers with high coercivity

Effect of Size Distribution on Magnetic Properties in Cobalt Nanowires

Self-Assembled Two-Dimensional Structure of Magnetic Cobalt Nanocrystals

Synthesis and Characterization of Metallic Co with Different Hierarchical Structures Prepared by A Simple Solvothermal Method

Synthesis of cobalt nanoparticles in ethanol hydrazine alkaline system (EHAS) at room temperature

Morphology Control of Magnetic Properties in Cobalt Nanowires

A Facile Aqueous Phase Synthesis of Cobalt Microspheres at Room Temperature

Synthesis and Characterization of Novel Three-Dimensional Metallic Co Dendritic Superstructures by a Simple Hydrothermal Reduction Route

Growth of dendritic antimony nanocrystals at room temperature