Abstract:A newly developed method for the formation of nanowires by self-aggregation of nanoparticles is presented in this paper. Co3C, Co-rich, and Ni nanoparticles dispersed on holey carbon grids are inserted in a vacuum oven and are co-annealed with PolyChloroTriFluoroEthylene (PCTFE) at 375 degrees C. No external electric or magnetic fields were applied. High resolution electron microscopy (HREM) was extensively used to determine the shape, size distribution and crystallographic phase of the starting and produced materials. Interestingly, after an annealing circle of 72 hours, the nanoparticles seem to self-agglomerate into nanowires which have diameters in the 5-20 nm range and lengths exceeding at cases 1 micron. The diameter of the produced wires is in the same range as the diameter of the initial nanoparticles, further supporting the notion that the nanowires have formed out of nanoparticle agglomeration. Close inspection of nanowire HREM images shows that the core structure of nanowires wider than approximately 11 nm resembles linked nanoparticles. Phase identification performed using the HREM images reveals the core is of the same phase/material as the starting nanoparticles. Since nanowires appear to form over holes on the holey carbon grid, a base growth mechanism is proposed. The fluorocarbon vapour decomposes over the transitional metal nanoparticles and carbon tubules start growing. The nanoparticles appear to be trapped inside the tubules where their close proximity enhances their fusion into a continuous core. At the studied temperature, the nanoparticle fusion is seen to be limited by the size of the nanoparticles manifested by continuous cores only in the thin nanowires. The process presented here shows that nanoparticles can spontaneously self-align into nanowires in a way and to an extent never reported before. Therefore there is certainly scope for studying this method further to reveal more information about the catalytic action of transitional metals on hydrocarbons and the exact nanowire formation mechanism. Although it is currently a matter of speculation, this process might lead to the effortless growth of nanowires at particular places when building miniature circuits.

Hydrothermal Microemulsion Synthesis of Cobalt Nanorods and Self-Assembly into Square-Shaped Nanostructures

Hydrothermal Synthesis of Self-Assembly Co Nanospheres and Their Magnetic Properties

Self-Assembled Two-Dimensional Structure of Magnetic Cobalt Nanocrystals

Hydrothermal synthesis of flower-like SrCO3 nanostructures

Simplified Synthesis of Single-Crystalline Magnetic CoFe2O4 Nanorods by a Surfactant-Assisted Hydrothermal Process

Functionalization of carbon nanotubes with magnetic nanoparticles: general nonaqueous synthesis and magnetic properties.

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

A Self-Assembly of Single Layer of Co Nanorods to Reveal the Magnetostatic Interaction Mechanism

Synthesis of Cobalt Nanowires by Template-Free Method

Spontaneous self-agglomeration of magnetic nanoparticles into nanowires

Hydrothermal Synthesis of Cobalt Particles with Hierarchy Structure and Physicochemical Properties

Magnetic field-induced solvothermal synthesis of one-dimensional assemblies of Ni-Co alloy microstructures

Facile hydrothermal synthesis of ZnCo2O4 nanostructures: controlled morphology and magnetic properties

Hydrothermal Synthesis and Structure Evolution of Hierarchical Cobalt Sulfidenanostructures

Hydrothermal self-assembling of ZnO nanorods into sphere-like superstructures and their optical characteristics

A Facile Hydrothermal Route to Spinel Coco2o4 Nanotubes and Porous Nanostructures Without Assisted Surfactants and Templates

Cobalt–iron cyanide hollow cubes: Three-dimensional self-assembly and magnetic properties

Chemical Synthesis, Structure and Magnetic Properties of Co Nanorods Decorated with Fe3O4 Nanoparticles

Synthesis and Formation Mechanism of Cobalt Compound Nanotubes

Cobalt hydroxide nanosheets and their thermal decomposition to cobalt oxide nanorings.

Synthesis And Magnetic Properties Of Zn1-Xcoxo Nanorods