Abstract:CdS nanorods of high aspect ratio were synthesized through the route of chemical bath deposition under a mild condition. Diphenylthiocarbazone (DPTA) was employed as an organic additive for the synthesis of CdS nanorods. The crystalline and microstructure of CdS nanorods were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns indicate the existence of both cubic and hexagonal phases in the samples. The sample with the pH value of 10.5 showed a hexagonal (111) peak of maximum intensity, indicating the preferential orientation along the c axis of hexagonal CdS phase. Meanwhile, the cubic phase appeared at the pH value of 10.5. The TEM images reveal that the morphology of CdS could be controlled by adjusting the pH value. Highly crystalline CdS nanorods with the diameter of about 50 nm and the length of about 3 mu m were obtained at the pH value of 10.5. The effects of the pH value on the formation of CdS nanorods were studied. The electrical properties of the samples were also investigated. The results show that the sample prepared with DPTA as the organic additive exhibited a much lower resistance than those prepared with PVA as the additive and in pure ethanol. There were two big pi bonds in a DPTA molecule, which benefited the electron transfer. Finally, the growth mechanism of CdS nanorods and electron transfer in DPTA modified CdS nanorods were discussed.

Single crystalline CdS nanorods fabricated by a novel hydrothermal method

Synthesis of Single Crystalline CdS Nanorods by a PVP-assisted Solvothermal Method

A Novel Hydrothermal Synthesis of Single Crystalline Pbs Nanorods and Their Characterization

Synthesis of One-Dimensional Chalcogenides by a Novel Hydrothermal Process

Two-dimensional SnS nanosheets fabricated by a novel hydrothermal method

Solvothermal Synthesis and Characterization of Uniform CdS Nanowires in High Yield

Synthesis of cadmium hydroxide nanoflake and nanowisker by hydrothermal method

Single-Crystalline Sns2 Nano-Belts Fabricated by A Novel Hydrothermal Method

Synthesis of CdS nanotubes by chemical bath deposition

Preparation and Growth Mechanism of CdS Nanorods via Chemical Bath Deposition

Self-assembly of CdS: from nanoparticles to nanorods and arrayed nanorod bundles

One-Step Fabrication of CdS Nanorod Arrays Via Solution Chemistry

Hydrothermal Preparation and Characterization of Cd0.9Mn0.1S Nanorods

Preparation of CdS Nanoparticles by Hydrothermal Method in Microemulsion

Hexagonal pencil-like CdS nanorods: Facile synthesis and enhanced visible light photocatalytic performance

Good Optical Properties of Branched CdS Nanoparticles and Its Large Area Growth via Solvothermal Route

Hydrothermal synthesis, characterization and properties of SnS nanoflowers

Hydrothermal synthesis of flower-like SrCO3 nanostructures

Some critical factors in the synthesis of CdS nanorods by hydrothermal process

Directional CdS Nanowires Fabricated by Chemical Bath Deposition

Formation Process of Cds Nanorods Via Solvothermal Route