Abstract:Manganese-substituted cobalt nano-ferrites, Co(1−x)Mn(x)Fe2O4 (x = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) were synthesized using chemical co-precipitation method. Physical properties of Co(1−x)Mn(x)Fe2O4 nano-ferrites were then characterized using thermal gravimetric—differential thermal analysis (TGA/DTA), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectrometer, transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). TGA/DTA study indicates that the thermal stability of the prepared manganese doped cobalt ferrite nanoparticles. X-ray diffraction patterns of all the prepared ferrite samples show good in quality, pure nanosized, single-phased cubical spinel structures, with ferromagnetic behavior. We demonstrated that the expansion of lattice constant (a) and crystallite size (D) induced by manganese substituted of cobalt ferrites exerted remarkable effects on its structural and magnetic properties. The lattice constant (a) and crystallite size (D) increase with increasing manganese substituted cobalt ferrites. Williamson–Hall (W–H) method was used to evaluate the crystallite size and lattice strain of the Co(1−x) Mn(x)Fe2O4 nanoparticles samples by peak broadening. The calculated crystal size of Co(1−x) Mn(x)Fe2O4 nanoparticles on the W–H plots were highly intercorrelated with the HR-TEM and results of Scherrer Deby equation. The other physical parameters, such as X-ray density, hopping length, ionic radius, bond length, tetrahedral edge, octahedral edge, and unshared octahedral edge values were estimated from the highest intensity peak (311) of X-ray diffraction. The Fourier transform infrared (FT-IR) spectrometer of the Co–Mn ferrite nanoparticles systems were recorded in the frequency range of 200–1000 cm−1. FT-IR spectra show the two fundamental absorption bands of interstitial sub-lattice sites (M–O). The high absorption band (ν1) and the low absorption band (ν2) corresponds to the tetrahedral [A] and octahedral (B) sites, respectively, confirming the formation of single cubic spinel ferrite lattice system. The TEM results show that the ferrite nanoparticles have a nearly spherical shape with some agglomerations. From the analysis of VSM, the values of saturation magnetization (Ms) increases from 31.46 to 37.16 emu/g, then decreases with increasing Mn2+ ions substitution in the Co-ferrite system. The coercivity of the Mn2+ ions substituted cobalt ferrites increases up to x = 0.6 followed by a decrease. The optimized magnetic parameters suggest that the material with composition Co0.6Mn0.4Fe2O4 may be suitable for longitudinal magnetic recording media and other various technological applications.

Enhanced magnetic properties of cobalt nanoparticles on FeMn films

Chemical synthesis and magnetic properties of monodisperse cobalt ferrite nanoparticles

Synthesis and influence of Zn substitution on optical and magnetic properties of cobalt ferrite nanoparticles by a polyacrylamide gel route

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Enhancement of magnetic properties in hard/soft CoFe2O4/Fe3O4 nanocomposites

Preparation and Magnetic Properties of Cobalt-Doped FeMn2O4 Spinel Nanoparticles

Synthesis-Dependent Structural and Magnetic Properties of Monodomain Cobalt Ferrite Nanoparticles

Magnetic homogeneity in Fe-Mn co-doped NiO nanoparticles

Thermal, microstructural and magnetic properties of manganese substitution cobalt ferrite prepared via co-precipitation method

Preparation and magnetic properties of cobalt doping Mn-Zn ferrite nanoparticles

Markedly Enhanced Coercive Field and Congo Red Adsorption Capability of Cobalt Ferrite Induced by the Doping of Non-Magnetic Metal Ions

Composition And Magnetic Properties Of Cobalt Ferrite Nano-Particles Prepared By The Co-Precipitation Method

Influence of Ce-Mn Co-Doping on the Structure and Magnetic Properties of Cobalt Ferrites

Synthesis of Cobalt Ferrite Nanoparticles and Effect of Doped Lanthanum on Magnetic Properties of Cobalt Ferrite

The magnetic properties and reversal of Fe–Co nanowire arrays

Magnetic properties of carbon coated Fe, Co and Ni nanoparticles

Diluted and undiluted monodispersed CoFe 2 O 4 nanoparticles: the effects of post-annealing on magnetic properties

Chemical Synthesis, Structure and Magnetic Properties of Co Nanorods Decorated with Fe3O4 Nanoparticles

Fabrication and magnetic properties of cobalt ferrite composite nanoparticles

Effect of Nitrogen and Cobalt Additions on Surface Morphology and Magnetic Properties of Fe Thin Films

Enhanced Magnetic Properties of Self-Assembled Fept Nanoparticles with Mno Shell