Thermal, microstructural and magnetic properties of manganese substitution cobalt ferrite prepared via co-precipitation method

Ali A. Ati,Alyaa H. Abdalsalam,Ali S. Hasan

DOI: https://doi.org/10.1007/s10854-020-05053-4

2021-01-18

Abstract:Manganese-substituted cobalt nano-ferrites, Co_{(1−<i>x</i>)}Mn_(<i>x</i>)Fe₂O₄ (<i>x</i> = 0.0, 0.2, 0.4, 0.6, 0.8 and 1.0) were synthesized using chemical co-precipitation method. Physical properties of Co_{(1−<i>x</i>)}Mn_(<i>x</i>)Fe₂O₄ nano-ferrites were then characterized using thermal gravimetric—differential thermal analysis (TGA/DTA), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectrometer, transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). TGA/DTA study indicates that the thermal stability of the prepared manganese doped cobalt ferrite nanoparticles. X-ray diffraction patterns of all the prepared ferrite samples show good in quality, pure nanosized, single-phased cubical spinel structures, with ferromagnetic behavior. We demonstrated that the expansion of lattice constant (<i>a</i>) and crystallite size (<i>D</i>) induced by manganese substituted of cobalt ferrites exerted remarkable effects on its structural and magnetic properties. The lattice constant (<i>a</i>) and crystallite size (<i>D</i>) increase with increasing manganese substituted cobalt ferrites. Williamson–Hall (W–H) method was used to evaluate the crystallite size and lattice strain of the Co_{(1−<i>x</i>)} Mn_(<i>x</i>)Fe₂O₄ nanoparticles samples by peak broadening. The calculated crystal size of Co_{(1−<i>x</i>)} Mn_(<i>x</i>)Fe₂O₄ nanoparticles on the W–H plots were highly intercorrelated with the HR-TEM and results of Scherrer Deby equation. The other physical parameters, such as X-ray density, hopping length, ionic radius, bond length, tetrahedral edge, octahedral edge, and unshared octahedral edge values were estimated from the highest intensity peak (311) of X-ray diffraction. The Fourier transform infrared (FT-IR) spectrometer of the Co–Mn ferrite nanoparticles systems were recorded in the frequency range of 200–1000 cm⁻¹. FT-IR spectra show the two fundamental absorption bands of interstitial sub-lattice sites (M–O). The high absorption band (<i>ν</i>₁) and the low absorption band (<i>ν</i>₂) corresponds to the tetrahedral [A] and octahedral (B) sites, respectively, confirming the formation of single cubic spinel ferrite lattice system. The TEM results show that the ferrite nanoparticles have a nearly spherical shape with some agglomerations. From the analysis of VSM, the values of saturation magnetization (<i>M</i>_s) increases from 31.46 to 37.16 emu/g, then decreases with increasing Mn²⁺ ions substitution in the Co-ferrite system. The coercivity of the Mn²⁺ ions substituted cobalt ferrites increases up to <i>x</i> = 0.6 followed by a decrease. The optimized magnetic parameters suggest that the material with composition Co_0.6Mn_0.4Fe₂O₄ may be suitable for longitudinal magnetic recording media and other various technological applications.