Ferromagnetic Co/SiO2 Core/shell Structured Nanoparticles Prepared by a Novel Aqueous Solution Method
XG Lu,GY Liang,ZB Sun,W Zhang
DOI: https://doi.org/10.1016/j.mseb.2004.11.012
IF: 3.407
2004-01-01
Materials Science and Engineering B
Abstract:Magnetic Co nanoparticles coated with silica were successfully synthesized using a novel aqueous solution method, and their structures and properties were studied by X-ray diffraction (XRD), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The experimental results showed that the size and the shape of the particles varied with the molar content of SiO2, reducing time and temperature. There was an optimum reducing time matching with SiO2 content at a certain reducing temperature. With the increase of SiO2 content, the reducing time should be increased too. The insulating layer of SiO2 can hinder nanoparticles from growing up. Two kinds of structures, f.c.c. Co and h.c.p. Co, could be found in the particles. The smaller the Co particles, the easier to obtain f.c.c. Co structure. And with increasing the reducing time and particles’ growing up, h.c.p. Co structure appeared. The spherical-shaped particles with average size about 10–150nm were dominant in these samples. However, some needle-shaped particles, which were about 70nm long and 10nm in diameter, also appeared in the samples with high SiO2 content. A relatively high saturation magnetization, 110–130emu/g or so, was obtained when the molar content of SiO2 was from 3 to 15mol%. The least coercivity of Co/SiO2 nanoparticles appeared in the sample with 8mol% SiO2, herein, the structure of particles was f.c.c. and the shape was spherical. With the increase of h.c.p. structure in the particles, the coercivity of nanoparticles increased.