Abstract:As the main candidates in the field of ultra-high temperature ceramics, high entropy carbides/borides (HECs/HEBs) have good oxidation resistance properties, high hardness, as well as excellent thermal and electrical conductivities, which are the focused points of research nowadays. In the current study, (Hf,Ta,Zr,Nb,Mo,Ti)C powders were successfully synthesized by a three-step process, including the mixing process of raw oxides and carbon black with spaying Fe(NO3)(3) solution, carbothermal reduction and subsequent calcium posttreatment. For the preparation of (Hf,Ta,Zr,Nb,Mo,Ti)B-2 powders, during the calcium posttreatment process, equal stoichiometric ratio of B4C was added for the purpose of boriding reaction. The relevant X-ray diffraction and SEM characterizations indicate the successful preparations of face-centered cubic HECs and hexagonal HEBs. However, slight Mo local segregation was found in the prepared (Hf,Ta,Zr,Nb,Mo,Ti)B-2 powders. The iron generated from Fe(NO3)(3) promotes the solid solution process between monocarbides during the carbothermal reduction process via the dissolution-diffusion-precipitation mechanism. In the calcium posttreatment process, the liquid calcium ensures the boriding reaction take place at a low temperature. In addition, the residual carbon could be combined with calcium to generate CaC2 which is easy to be removed by acid leaching, and meanwhile, the added Fe could also be finally eliminated to produce pure HEC/HEB powders. The current method does not require the long-time high energy ball milling of raw materials, but only simple and mild mixing is enough. Therefore, such a facile route has a great potential application prospect for industrially preparing high entropy phase powders in a large scale.

A Thermal Reduction Route to Nanocrystalline Transition Metal Carbides from Waste Polytetrafluoroethylene and Metal Oxides

One Step Conversion Of Waste Polyethylene To Cr3c2 Nanorods And Cr2alc Particles Under Mild Conditions

A New Reduction-Carburization Route to Nanocrystalline Tic

In-situ Synthesis of Nanocrystalline TiC Powders, Nanorods, and Nanosheets in Molten Salt by Disproportionation Reaction of Ti(II) Species

Synthesis of Metastable Ternary Pd-W and Pd-Mo Transition Metal Carbide Nanomaterials

Synthesis and Characterization of TiC Nanofibers Obtained via a Modified Carbothermal Process

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

A practical guideline for designing high-entropy carbides based on (Ti1/3Mo1/3W1/3)C with high valence electron concentration

Synthesis and Oxidation Behavior of Nanocrystalline Niobium Carbide

A Facile Route for the Synthesis of High‐entropy Transition Carbides/borides at Low Temperatures

The co-reduction route to TiC nanocrystallites at low temperature

Low-Temperature Fabrication of TiC Nanotube Arrays by Molten Salt Electrolysis for Supercapacitor Application

Converting Waste Polyethylene into ZnCCo3 and ZnCNi3 by a One-Step Thermal Reduction Process.

Formation Of Nanocrystalline Tic By A Low-Temperature Route

A Simple Route for the Direct Conversion of Waste Plastic to Hafnium Carbide Nanoparticles at Low Temperature

Phase controlled synthesis of transition metal carbide nanocrystals by ultrafast flash Joule heating

A co-reduction synthesis of superconducting NbC nanorods

Synthesis of Tungsten Carbide Nanocrystal Via A Simple Reductive Reaction

Cr-assisted Low-Temperature Densification of (ti,zr,nb,ta,mo)c High-Entropy Carbides with Ultrafine Grain and Enhanced Hardness

Carbide Nanoparticles Encapsulated in the Caves of Carbon Nanotubes by an in Situ Reduction-Carbonization Route

A Simple Route to Prepare Nanocrystalline Titanium Carbonitride