Abstract:Niobium carbide (NbC) is a high-field Type II superconductor with a critical temperature ($T_C$) of 11.1 K, just above that of pure Nb ($T_C = 9$ K). Downsizing NbC to the nanoparticle scale introduces significant alterations in its critical field and/or the superconducting temperature. Here we report on superconducting NbC nanoparticles with $T_C \approx$ 10 K synthesized by laser ablation in acetone, using the lens-target distance (laser fluence) and centrifugation as control parameters of the particle size. X-ray diffraction analyses certified the cubic NbC phase and electron microscopy images revealed spherical particles with average size near 8 nm, with no apparent size dependence on fluence. Besides, magnetization curves exhibited magnetic loops featuring a saturation magnetization around $10^{-3} \mu_B$/molecule along with a small and typical superconducting loop for all investigated samples. We also observed a suppression of the diamagnetic behavior below $T_C$ upon decreasing laser fluence. Moreover, all samples exhibited a weak electron spin resonance (ESR) Curie-like signal at $g\approx2.0$ probably associated with localized defects in the particle's surface. The intriguing coexistence of superconductivity and magnetism in nanoparticles has recently garnered significant research attention. This complex scenario and unique properties are due to the substantial increase of surface-to-volume ratio in these superconducting NbC nanoparticles and further investigation would be crucial to unveil novel material properties and shed new light on our understanding of the superconducting phenomenon in this new morphology.

A co-reduction synthesis of superconducting NbC nanorods

Low temperature synthesis of NbB2 nanorods by a solid-state reaction route

Synthesis and Characterization of Superconducting NbC Nanotubes

Synthesis and characterization of superconducting nanocrystalline niobium nitride.

The co-reduction route to TiC nanocrystallites at low temperature

Synthesis of ZrC hollow nanospheres at low temperature

A Co-reduction-carburization Route to Synthesize Nanocrystalline ZrC

Superconductivity and Fermi-surface nesting in the candidate Dirac semimetal NbC

Vacuum encapsulated synthesis of 11.5 K NbC superconductor

Preparation of Nb 3 Al Superconductor by Powder Metallurgy and Effect of Mechanical Alloying on the Phase Formation

Synthesis and Oxidation Behavior of Nanocrystalline Niobium Carbide

Nanoparticles of NbC produced by laser ablation in liquid: a study of structural, magnetic and superconductivity properties

Formation of TaC Nanorods with a Low-Temperature Chemical Route

A Thermal Reduction Route to Nanocrystalline Transition Metal Carbides from Waste Polytetrafluoroethylene and Metal Oxides

A Simple Route to Prepare Nanocrystalline Titanium Carbonitride

A facile molten salt route to K2Nb8O21 nanoribbons

Reduction–boronation Route to Chromium Boride (crb) Nanorods

A Novel Route To Multiwalled Carbon Nanotubes And Carbon Nanorods At Low Temperature

A Chemical Co-Reduction Route to Synthesize Nanocrystalline Vanadium Carbide

A low temperature synthesis of crystalline B4C ultrafine powders

A New Reduction-Carburization Route to Nanocrystalline Tic