Abstract:To improve the ablation resistance of carbon/carbon (C/C) composites, tungsten (W) coating with thickness of 1.2 mm was applied by atmospheric plasma spraying. The antiablation property of the coated composites was evaluated by oxyacetylene flame ablation experiments. The phase composition of the coating was investigated by a combination of x-ray diffraction analysis and scanning electron microscopy with energy-dispersive x-ray spectroscopy analysis. The ablation resistance of the coated C/C substrates was compared with that of uncoated C/C composites and C/C-CuZr composites after ablation for 30 s. The properties of the coated C/C composites after ablation time of 10, 30, 60, 90, 120, and 180 s were further studied. The results indicated that the mass and linear ablation rates of the W-coated C/C composites were lower than those of uncoated C/C or C/C-CuZr composites after ablation for 30 s. The coating exhibited heat stability after 120 s of ablation, with mass loss and linear ablation rates of 7.39 × 10 −3 g/s and 3.50 × 10 −3 mm/s, respectively. However, the W coating became ineffective and failed after ablation for 180 s. Three ablation regions could be identified, in which the ablation mechanism of the coating changed from thermochemical to thermophysical erosion to mechanical scouring with increasing ablation time.

Ablation Behavior of HfC Protective Coatings for Carbon/carbon Composites in an Oxyacetylene Combustion Flame

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Cyclic ablation behavior and microstructure evolution of multi-layer coating on C/C composites under oxyacetylene torch

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation Resistance of C/C Composites with Atmospheric Plasma-Sprayed W Coating

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Oxidative ablation behavior of W‐coated C/C composites prepared by CVD with heat‐treatment

Effect of HfC addition on ablation behavior of SiBCN ceramics

Ablation and mechanical behaviour of C/C composites under an oxyacetylene flame and tensile loading environment

Oxidative Ablation Behavior of W‐Coated C/C Composites Prepared by Chemical Vapor Deposition with Heat Treatment

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Microstructure and ablation performance of HfC/PyC core-shell structure nanowire-reinforced Hf1-xZrxC coating

Ablation behaviors of ultra-high temperature ceramic composites