Abstract:Carbide coatings are very important in molding industries due to their good anti-wear properties increasing the life of molds of hot and cold forging, extrusion and powder metallurgy exposing to abrasive forces. Diverse processes are applied to produce carbide coatings. One of them is the thermo-reactive diffusion method (TRD) using a molten salt bath. This process has many advantages including cost-effectiveness over other similar surface coating methods. The aim of this study is the formation of carbide-composite coatings using molten salt baths containing oxides of carbide forming elements individually and in a mixed form on SKD-11 cold work tool steel at 1000 degrees C. For this purpose, two sets of experiments were considered in this study. In experiment A, a chromium oxide bath and then a mixed chromium oxide and vanadium oxide bath with a molar ratio of Cr to V equal to 0.66 were used. In experiment B, at first a mixed chromium oxide and vanadium oxide bath (Cr/V ratio = 0.66) and next a single bath of vanadium oxide were utilized. To evaluate and compare the produced coatings, FE-SEM, EPMA (point, line and map), XRD analysis, nano-indentation and wear tests were performed. The results showed that the coatings include chromium carbides (Cr3C2, Cr7C3 and Cr23C6) and vanadium carbides (V2C, V6C5 and V8C7) as well as a carbon-chromium-vanadium triple phase with the composition of Cr2C2V. Moreover, the best hardness and abrasion resistance were gained for the coating produced in the molten bath containing chromium oxide and vanadium oxide after experiencing a chromium oxide bath. For the sample, the hardness was between 17.2 and 19.6 GPa and the lowest amount of COF was 0.32.

Thermo-reactive deposition processed vanadium carbide coating: Growth kinetics model and diffusion mechanism

Evaluation of Vanadium Carbide Coatings on AISI H13 Obtained by Thermo-Reactive Deposition/diffusion Technique

On the Formation and Properties of Chromium Carbide and Vanadium Carbide Coatings Produced on W1 Tool Steel Through Thermal Reactive Diffusion (TRD)

The microstructure evolution of VC coatings on AISI H13 and 9Cr18 steel by thermo-reactive deposition process

A kinetic description of Vanadium carbide coating formed by the plasma electrolytic method

Growth Kinetics and Microstructure of Composite Coatings on H13 by Thermal Reactive Diffusion

INVESTIGATION OF CHROMIUM AND VANADIUM CARBIDE COATING FORMATION ON SKD11 AND T10 BY THERMO-REACTIVE DIFFUSION (TRD) METHOD

Tribological Properties of Duplex Coatings of Chromium-Vanadium Carbide Produced by Thermo-Reactive Diffusion (TRD)

Characterization of gradient vanadium carbide coating using synchrotron X-ray microdiffraction

Investigation of Chromium and Vanadium Carbide Composite Coatings on CK45 Steel by Thermal Reactive Diffusion

Fabrication and Dynamics of Two Layers Vanadium Carbide Reinforced Iron Matrix Surface Composite

A Kinetic Model for the Initial Growth of Diamond Films

Experimental Study and Computer Simulation on Multicomponent Diffusion in Multiphase Dispersions During Solid Carburizing of HP40Nb and KHR45A Alloys

Microstructure and Formation Mechanism of Vanadium Carbide-Reinforced Iron-Matrix Composites Prepared by Solid-Phase Diffusion

Modeling the Reactive Sputter Deposition of Ti-doped VO X Thin Films

Strain-Induced Precipitation Kinetics of Vanadium Carbonitride Precipitates with the Cubic Structure in High-Strength Weathering Steels

Effect of V on the Precipitation Behavior of Ti−Mo Microalloyed High-Strength Steel

Cobalt Diffusion During the Initial Stage of CVD Diamond Growth on Cemented Carbide – A Molecular Dynamics and Experimental Study

Diffusion mechanism in molten salt baths during the production of carbide coatings via thermal reactive diffusion

Growth and mechanical properties of Nb-Cr carbide coatings on graphite by TRD technique

Growth behavior of CVD Ti(C,N,O) coating on cemented carbide controlled by CO and the mechanism