Abstract:Direct ink writing (DIW) and low-temperature sintering methods were applied to prepare Si2N2O-Si3N4 ceramics for radome materials. Lattices of Si-SiO2 green body were printed by DIW with 78 wt % solid portion of water-based Si-SiO2 slurry, in which silicon particles and silica fume were used as the solid portion and Methylcellulose (HPMC) was used as the dispersant. Effects of HPMC addition on stability and silica fume content on rheological properties of the slurry were studied, respectively. The pseudoplastic mechanism of the slurry was analyzed. The Si-SiO2 green bodies were sintered at 1250 °C–1400 °C in nitrogen. The effect of temperature on phase composition, microstructure, mechanical and dielectric properties of samples was investigated. With the HPMC addition of 0.12 wt% and the silica fume proportion of 30 wt% in solid portion, a stable and pseudoplastic slurry with the yield stress of 110.9 Pa was obtained, which is suitable for DIW. With the decrease of initial holding temperature, more N2 enters the sample and reacts with silicon and silica fume, promoting the generation of Si2N2O and Si3N4. The optimal condition yields Si2N2O-Si3N4 ceramics with apparent porosity of 42.73%, compressive strength of 24.7 MPa, dielectric constant of 4.89 and loss tangent of 0.0054. It is found that columnar Si3N4 comes from a direct reaction between silicon and N2, and fibrous Si2N2O is mainly generated by the reaction between silicon, SiO(g), and N2 through the chemical vapor deposition mechanism. Good dielectric properties are achieved due to high porosity, high proportion of Si2N2O phase and no residual silicon.

Preparation of Si 3N 4 foam ceramics with nest-like cell structure by particle-stabilized foams

Pore Structure Control of Si3n4 Ceramics Based on Particle-Stabilized Foams

A Novel Method of Strong and Tough Si3N4 Ceramic from the Particle‐stabilized Foam

Preparation of Si3N4 Foam Ceramics Using Short-Chain Amphiphile

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Formation of hierarchical Si3N4 foams by protein-based gelcasting and chemical vapor infiltration

Study on particle-stabilized Si3N4 ceramic foams

Factors affecting the microstructure of a fine ceramic foam

Ultralight Silicon Nitride Ceramic Foams from Foams Stabilized by Partially Hydrophobic Particles

Facile Fabrication of Nanofibrous Network Reinforced Hierarchical Structured Porous Si3N4-based Ceramics Based on Si-Si3N4 Binary Particle-Stabilized Foams

Manufacture of Si3N4-SiCN composite bulks with hierarchical pore structure

In Situ Synthesis of Three-Dimensional Nanofiber-Knitted Ceramic Foams Via Reactive Sintering Silicon Foams

Fabrication and properties of Si2N2O-Si3N4 ceramics via direct ink writing and low-temperature sintering

Novel porous Si3N4 ceramics prepared by aqueous gelcasting using Si3N4 poly-hollow microspheres as pore-forming agent

Effect of carboxymethyl cellulose addition on the properties of Si3N4 ceramic foams

SiC–Si3N4 composite with multi-laminate nanowires originated from oriented porous structure by freeze-casting

Directly Growing Nanowire-Assembled Nanofibrous Ceramic Foams with Multi-Lamellar Structure Via Freeze-Casting Process

Ultralight and Mechanically Robust SiC Foams with Interconnected Cellular Architecture

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Preparation and Performance of Si3N4 Hollow Microspheres by the Template Method and Carbothermal Reduction Nitridation

Porous Si3N4-based Ceramics with Uniform Pore Structure Originated from Single-Shell Hollow Microspheres