Effect of Alloying Elements on Microstructure and Aging Hardening Behaviors of Mg-Gd Based Alloys
Li Luran,Sun Wei,Liu Linlin
DOI: https://doi.org/10.3969/j.issn.0258-7076.2012.01.004
2012-01-01
Abstract:SEM and TEM observations were applied to investigate the microstructures of as-solidified and solution-treated MgGd3(%,atom fraction),MgGd3Nd0.3(%,atom fraction) and MgGd3Nd0.3Zn0.3(%,atom fraction) alloys,and microhardness testing carried out to characterize the age-hardening behaviors of the solution-treated alloys at 200 ℃ as well.The results showed that MgGd3,MgGd3Nd0.3 and MgGd3Nd0.3Zn0.3 alloys were all age hardenable,in which the as-cast RE-rich primary phases could be solutionized significantly after heat treated at 520 ℃.For all these alloys,reaching their peak hardness during aged at 200 ℃ was associated with the formation and dispersive distribution of fine β′-phases of high volume fraction,while their hardness variations after the peak aging stage exhibited obviously different tendencies.As a result of introducing Nd to MgGd3 and thus realizing the precipitation strengthening with both Gd and Nd involved,the MgGd3Nd0.3 alloy,with aging response being improved significantly,could have aging hardness higher than the other two alloys during aged for 0～120 h.The addition of Zn could retain adequate high hardness,without decreasing tendency,for the MgGd3Nd0.3Zn0.3 alloy after aged for a long period of time,even though its peak hardness was slightly lower than that of the MgGd3Nd0.3 alloy.By means of TEM observations,the microstructural comparison of the three alloys aged at 200 ℃ for 85 h was focused,through which the formation of precipitates,their sizes,morphology and distribution in these aged alloys would be reported and the effects of Nd and Zn additions on these features would be discussed.