Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Synthesis of Monodispersed La2Ce2O7 Nanocrystals Via Hydrothermal Method: A Study of Crystal Growth and Sintering Behavior

Investigation of Growth, Structural and Optical Properties of CeO2 Nanocrystalline Thin Films Prepared by Pulsed Spray-Evaporation Chemical Vapor Deposition (PSE-CVD)

Secondary Phase CeO2 Precipitates in Ce,Er-Doped Na0.5La0.5MoO4 Single Crystals Grown by Czochralski Method

Preparation, Characterization, And Thermophysical Properties Of (La0.95sr0.05)(2)Ce2o6.95 Ceramic For Thermal Barrier Coatings

Preparation and Thermal Conductivity of (La0.95Mg0.05)2Ce2O6.95 Ceramics

Synthesis and microstructure of La-doped ceria nanoparticles.

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Preparation of Ce-doped (y,gd)3al5o12 Nanoceramics by Sintering and Crystallization of Glass Microspheres

Hydrothermal synthesis of CeO2 nano-particles

Synthesis of Nanocrystalline Ce<sub>0.8</sub>Sm<sub>0.2</sub>O<sub>1.9</sub> by Citrate Gel Method

Preparation and Characterization of Nanocrystalline Gd2sio5 : Ce

Sintering of high-entropy nanoparticles obtained by polyol process: A case study of (La0.2Y0.2Nd0.2Sm0.2Gd0.2)2Ce2O7-δ

Synthesis of Nanocrystalline Ce0.8sm0.2o1.9 by Citrate Gel Method

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Controllable synthesis of spherical cerium oxide particles

Controlled Hydrothermal Synthesis of CeO2 Nanoparticles, Their Photocatalytic Activity and Room Temperature Ferromagnetism

Low-Temperature Preparation of Dense 10 Mol%-Y2o3-Doped Ceo2 Ceramics Using Powders Synthesized Via Carbonate Coprecipitation

Synthesis of nanocrystalline Ce0.8Sm0.2O 1.9 by citrate gel method

Synthesis and Characterization of Ceo2 by the Hydrothermal Method Assisted by Carboxymethylcellulose Sodium

Shape-selective Synthesis and Oxygen Storage Behavior of Ceria Nanopolyhedra, Nanorods, and Nanocubes.

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method