Abstract:A series of FeMnTiOx mixed oxides catalysts, which were synthesized by a CTAB-assisted co-precipitation process and calcined at different temperatures, were investigated for selective catalytic reduction of NO with NH3 in the presence of excess O-2. The samples were characterized by means of N-2-physisorption, XRD, TEM, H-2-TPR, XPS, NH3-TPD, and in situ DRIFTS technologies. The results indicated that the activities of samples were not predominately determined by BET specific surface area. Compared with amorphous TiO2, the anatase TiO2 crystalline phase was more conducive to enhance the electron interaction between manganese species and support: Mn4+ + Ti3+ <-> Mn3+ + Ti4+center dot NH3 was easier to be activated on the surface of samples which had lower binding energy of lattice oxygen in selective catalytic reduction of NO with NH3. The addition of CAB not only promoted the formation of anatase TiO2 crystalline phase and Lewis acid sites, but also improved the dispersion extent of active phase on the surface of samples. Thus, it enhanced the catalytic performance of samples. In addition, calcination temperature had an important influence on the valence state of manganese species, as well as the dispersion extent of active phase and the crystal phase structure of support. The sample calcined at 4000 degrees C showed excellent low-temperature activity and mid-temperature N-2 selectivity. The NO conversion and N-2 selectivity of this sample were above 90% in the range of 150-350 degrees C at a space velocity of 30,000 mL g(-1) h(-1). Furthermore, it exhibited sulfur tolerance and water resistance to a certain extent. (C) 2015 Elsevier B.V. All rights reserved.

Direct Synthesis, Characterization and Catalytic Performance of Bimetallic Fe–Mo-SBA-15 Materials in Selective Catalytic Reduction of NO with NH3

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Direct Synthesis, Characterization and Catalytic Performance of Al–Fe-SBA-15 Materials in Selective Catalytic Reduction of NO with NH3

Catalytic Performance of Bimetallic Systems (Cu-Fe, Cu-Mn, Fe-Mn) Based on Spherical MCM-41 Modified by Template Ion-Exchange in NH3-SCR Process

Understanding the high performance of an iron-antimony binary metal oxide catalyst in selective catalytic reduction of nitric oxide with ammonia and its tolerance of water/sulfur dioxide

Synthesis of Bimetallic MOFs MIL-100(Fe-Mn) As an Efficient Catalyst for Selective Catalytic Reduction of NO X with NH 3

Studies on Surface Structure of MxOy/MoO3/CeO2 System (m=ni, Cu, Fe) and Its Influence on SCR of NO by NH3

Synthesis and characterization of mesoporous Mn/Al-SBA-15 and its catalytic activity for NO reduction with ammonia

Activity and Characterization of Ce–Mo–Ti Mixed Oxide Catalysts Prepared by a Homogeneous Precipitation Method for Selective Catalytic Reduction of NO with NH3

Bimetallic Cerium–copper Nanoparticles Embedded in Ordered Mesoporous Carbons As Effective Catalysts for the Selective Catalytic Reduction of NO with NH3

A Novel MnOx–MoOx Codoped Iron-Based Catalyst for NH3-SCR with Superior Catalytic Activity over a Wide Temperature Range

Effect of Metal Complexing on Mn–Fe/TS-1 Catalysts for Selective Catalytic Reduction of NO with NH3

Synthesis, Characterization and Catalytic Performance of Femntiox Mixed Oxides Catalyst Prepared by A Ctab-Assisted Process for Mid-Low Temperature Nh3-Scr

Promotional effect of aluminum doping on the sulfated Fe2O3 catalyst in selective catalytic reduction of NO with NH3

Study on the selective catalytic reduction of NO by C3 H6 with metal organic material MOF-5

On the performance of Fe-Cu-ZSM-5 catalyst for the selective catalytic reduction of NO with NH3: the influence of preparation method

Catalytic Performance and Sulfur Dioxide Resistance of One-Pot Synthesized Fe-MCM-22 in Selective Catalytic Reduction of Nitrogen Oxides with Ammonia (NH3-SCR)-The Effect of Iron Content

Synthesis, characterization and catalytic performances of Cu- and Mn-containing ordered mesoporous carbons for the selective catalytic reduction of NO with NH3

Comprehensive understanding of the superior performance of Sm-modified Fe2O3 catalysts with regard to NO conversion and H2O/SO2 resistance in the NH3-SCR reaction

Promoting effect of Cu and Mn doping on the Fe/ZSM-5 catalyst for selective catalytic reduction of NO with NH 3