Abstract:A series of FeMnTiOx mixed oxides catalysts, which were synthesized by a CTAB-assisted co-precipitation process and calcined at different temperatures, were investigated for selective catalytic reduction of NO with NH3 in the presence of excess O-2. The samples were characterized by means of N-2-physisorption, XRD, TEM, H-2-TPR, XPS, NH3-TPD, and in situ DRIFTS technologies. The results indicated that the activities of samples were not predominately determined by BET specific surface area. Compared with amorphous TiO2, the anatase TiO2 crystalline phase was more conducive to enhance the electron interaction between manganese species and support: Mn4+ + Ti3+ <-> Mn3+ + Ti4+center dot NH3 was easier to be activated on the surface of samples which had lower binding energy of lattice oxygen in selective catalytic reduction of NO with NH3. The addition of CAB not only promoted the formation of anatase TiO2 crystalline phase and Lewis acid sites, but also improved the dispersion extent of active phase on the surface of samples. Thus, it enhanced the catalytic performance of samples. In addition, calcination temperature had an important influence on the valence state of manganese species, as well as the dispersion extent of active phase and the crystal phase structure of support. The sample calcined at 4000 degrees C showed excellent low-temperature activity and mid-temperature N-2 selectivity. The NO conversion and N-2 selectivity of this sample were above 90% in the range of 150-350 degrees C at a space velocity of 30,000 mL g(-1) h(-1). Furthermore, it exhibited sulfur tolerance and water resistance to a certain extent. (C) 2015 Elsevier B.V. All rights reserved.

Synthesis and characterization of mesoporous Mn/Al-SBA-15 and its catalytic activity for NO reduction with ammonia

Direct Synthesis, Characterization and Catalytic Performance of Al–Fe-SBA-15 Materials in Selective Catalytic Reduction of NO with NH3

Direct Synthesis, Characterization and Catalytic Performance of Bimetallic Fe–Mo-SBA-15 Materials in Selective Catalytic Reduction of NO with NH3

Synthesis, characterization and catalytic performances of Cu- and Mn-containing ordered mesoporous carbons for the selective catalytic reduction of NO with NH3

Synthesis, Characterization and Catalytic Performance of Femntiox Mixed Oxides Catalyst Prepared by A Ctab-Assisted Process for Mid-Low Temperature Nh3-Scr

Structures and Catalytic Performances of Me/SAPO-34(Me=Mn,Ni,Co) Catalysts for Low-Tem Perature SCR of NO X by Ammonia

Structures and catalytic performances of Me/SAPO-34 (Me = Mn, Ni, Co) catalysts for low-tem perature SCR of NO by ammonia

Preparation, Characterization, and Catalytic Performance of High Efficient CeO2-MnOx-Al2O3 Catalysts for NO Elimination

Synthesis and characterization of Mn3O4 and Mn2O3 nanocrystals on SBA-15: Novel combustion catalysts at low reaction temperatures

Characterization and Performance of Pt/SBA-15 for Low-Temperature SCR of NO by C3H6

Mesoporous MnOx-CeO2 composites for NH3-SCR: the effect of preparation methods and a third dopant

Fe-MCM-41 from Coal-Series Kaolin as Catalysts for the Selective Catalytic Reduction of NO with Ammonia

Tunable Highly Dispersed Nia-xMnxAlOy Catalysts Derived from Layered Double Oxide for Low Temperature NOx Removal

Experimental and Theoretical Investigation of Mesoporous MnO2 Nanosheets with Oxygen Vacancies for High-Efficiency Catalytic DeNO(x)

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Synthesis of Mn-Fe/γ-Al2O3 and Its Performance in Catalytic Oxidation of NO

Cu-SAPO-17: A novel catalyst for selective catalytic reduction of NO

Catalytic oxidation of NO over SmMn2O5 nanostructures derived from different Mn precursors

Unveiling the SO 2 Resistance Mechanism of a Nanostructured SiO 2 ( x )@Mn Catalyst for Low-Temperature NH 3 -SCR of NO

Sm-MnO catalysts for low-temperature selective catalytic reduction of NO with NH3: Effect of precipitation agent

Spinel Structured CoaMnbOx Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3