Microstructure characterization and mechanical properties of TiB 2/TiAl in situ composite by induction skull melting process

Hongzhi Niu,Shulong Xiao,Fantao Kong,Ce Zhang,Yuyong Chen

DOI: https://doi.org/10.1016/j.msea.2011.11.017

2012-01-01

Abstract:Microstructures and mechanical properties of Ti-45Al-2Nb-1.5V-1Mo-0.3Y+3vol% TiB 2 in situ composite fabricated by induction skull melting (ISM) process were investigated. Results showed that ISM process is feasible to fabricate high-quality in situ TiB 2/TiAl composite. The composite exhibits much finer lamellar colony size and lamellar spacing, compared with its TiAl base. Hexagonal primary and needlelike second TiB 2 particles uniformly distribute mainly near lamellar colony boundaries with a few inside lamellar colonies. TiB 2 crystals in current TiAl composite exhibit faceted growth mode along [0001] direction. The diverse morphologies of TiB 2 are principally ascribed to intrinsic crystal structure and different growth stages during solidification. This composite exhibits much better tensile strength and ductility than its TiAl matrix, with tensile strength (UTS) 610MPa and elongation (e{open}) 0.7% at room temperature, and UTS 505MPa and e{open} 12% at 800°C, respectively. © 2011.