Abstract:In the present study, ZrB2 nanoparticles were synthesized using sol-gel method. Zirconium alkoxide was used as the source of zirconium and boric acid as the source of boron. The size of precursor nanoparticle was controlled using the pH parameter inside the sol, and the formation of primary nuclei of ZrB2 phase and their crystallized amount were investigated using the temperature parameter. To evaluate the mechanism of product formation during the sol-gel process, TEM, SEM, DTA/TG, RAMAN, XRD, FTIR, and DLS methods were used. DLS analysis showed that the size of precursor particle inside the sol at pH less than 5 was below 10 nm. Measurements of viscosity and zeta potential inside the sol showed that in the acidic range, the particle stability decreases with increasing pH. Mixing of precursor particles at molecular level inside the sol was one of the important reasons in reducing the synthesis temperature of ZrB2 particles. FTIR analysis on chemical bonds showed that Zr-O-B bond was formed inside the gel powder. DTA analysis showed that the primary nuclei of ZrB2 particles were formed at a temperature of about 1400 °C. XRD observations proved that the primary nuclei of the ZrB2 phase crystallized and grew at a temperature of about 1500 °C. Surface research revealed that the specific surface area of the synthesized ZrB2 particles is equivalent to 115 m2/g, and also the surfaces of these particles are porous, and the size of these porosities is in meso range. SEM analysis showed that the particle size of ZrB2 having homogeneous morphology is about 50 nm. TEM microstructural analysis revealed that ZrB2 particles were formed uniformly and orderly in very fine dimensions.Graphical abstract

Effects of Sol Network Modifiers on Preparation, Morphology and Phase Composition of Zirconium Diboride Nano-Powders by Novel Sol-Gel Technology

Preparation of Zirconia Powders by Sol-gel Process

Preparation of Zirconium Diboride Nanopowders Using Different Zirconium Sources Via Sol-Gel Method

Synthesis of Zirconium Diboride Nano-Powders by Novel Complex Sol–gel Technology at Low Temperature

Low-temperature Synthesis of ZrB2 Nano-Powders Using a Sorbitol Modified Sol–gel Processing Route

Zirconium diboride powders synthesized by boro/carbothermal reaction using sol-gel technology

Synthesis of Ultra-Fine Zirconium Diboride Powders by Sol-Gel and Precursor Pyrolysis Method

Morphology evolution of ZrB2 nanoparticles synthesized by solgel method

Improvement of ZrB2 nanopowder synthesis by sol-gel method via zirconium alkoxide/boric acid precursors

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Synthesis of Ultrafine ZrB2 Powders by Sol-Gel Process

Synthesis of ZrB 2 nanoparticles by sol-gel method

Synthesis of ZrB_2 Powder by Wet Chemical Method

Preparation of t-ZrO2 by a sol–gel process with carbon as a phase transformation promoter

Synthesis of Ultra-Fine and High-Pure Zirconium Diboride Powders Using Solution-Based Processing

Synthesis of Ultra-fine Zirconium Diboride Powders by Liquid-phase Method

Preparation of Zirconia Nanopowders in Ultrasonic Field by the Sol-Gel Method

Carbothermal Reduction Acted Synergistically with Sol.Gel Method to Synthesize ZrB2 Nanoparticles

A New Preparation Method of Nanometer Zirconium Oxide

Nano-Dispersed 8 Mol% Yttria Stabilized Zirconia Powder: Phase, Morphology and Conductivity Investigation with Different Chelating Agents Via Modified Sol-Gel Method