Abstract:Porous Si3N4 ceramics are widely applied in many fields owing to their excellent properties such as high electromagnetic wave permeability, oxidation resistance, and wear resistance. Besides, the vat photopolymerization (VPP) technique can fabricate porous Si3N4-based ceramics with complex shapes and high precision. Nevertheless, The high absorptivity and refractive index of Si3N4 to ultraviolet light make it difficult to form porous Si3N4-based ceramics with the VPP technique. In this work, the addition of ZrO2 simultaneously improved the printability of Si3N4 slurries and the performance of Si3N4 ceramics via VPP technology. Rheological behavior and curing properties of the slurries were investigated, and the influence of ZrO2 content on the mechanical properties of printed Si3N4-based ceramics was investigated systematically. The addition of ZrO2 decreased the UV absorptivity of composite powder, thus improving the curing depth from 25.2 +/- 2.6 mu m to 64.8 +/- 3.7 mu m. XRD analysis revealed that ZrO2 in the composite ceramics mainly exists as the phase of yttria-stabilized tetragonal zirconia (Zr0.92Y0.08O1.96), which could ensure the effect of phase transformation toughening. With the increase of ZrO2 content, flexural strength and fracture toughness of porous Si3N4-based ceramics exhibited a trend of increase first and then decrease. As ZrO2 content increased to 10 wt%, the flexural strength and fracture toughness of porous Si3N4-based ceramics were improved from 214.7 MPa and 4.23 MPa center dot m1/2 to 345.0 MPa and 5.69 MPa center dot m1/2, respectively. Therefore, this work provided an important reference for the fabrication of highperformance porous Si3N4-based ceramic components with complex structures.

Preparation and Characterization of Functional Gradient Porous Zro2 Ceramics

In Vitro Cell Proliferation and Mechanical Behaviors Observed in Porous Zirconia Ceramics.

Preparation and Characterization of Fibrous Alumina and Zirconia Toughened Alumina Ceramics with Gradient Porosity

Highly Interconnected and Functionally Graded Porous Bioceramics

Porosity effect on the functional properties and energy harvesting performance of Ba0.85Ca0.15Ti0.90Zr0.10O3 ceramics

Preparation of Porous Spodumene/zircon Composite Ceramics and Its Thermal and Mechanical Properties

Mechanical analysis and fabrication of the bioinspired functionally graded interface layer of all-ceramic restoration

Additive Manufacturing of Gradient Porous Si/SiC Ceramic Parts: Quasi-static Behaviors and Mechanical Properties

Preparation and Properties of Porous ZTM Ceramics

Preparation and stereolithography 3D printing of ultralight and ultrastrong ZrOC porous ceramics

Zirconia-Toughened Alumina (ZTA) Nanoceramics with a Gradient Microstructure: A Comparative Study of ZTA Ceramics with Fibrous and Granular Morphology

Preparation and performance of zirconium oxide-toughened hydroxyapatite nano-composite porous bioceramic

Preparation of Porous SiC Ceramics Skeleton with Low-Cost and Controllable Gradient Based on Liquid Crystal Display 3D Printing

Microstructure and permeability of porous YSZ ceramics with aligned and gradient pore channels fabricated by freeze casting

ZrO2 Reinforced Porous Si3N4-based Ceramics with Improved Mechanical Properties Fabricated Via Vat Photopolymerization (VPP)

Synthesis and Characteristic of Hierarchically Porous Zirconium Oxide Doped with Yttrium

Preparation and Characterization of YSZ Porous Ceramic Tubes with a High Porosity by Wet Method

Preparation of Mesoporous Bioglass Coated Zirconia Scaffold for Bone Tissue Engineering

Preparation of Pore-Controllable Zirconium Carbide Ceramics with Tunable Mechanical Strength, Thermal Conductivity and Sound Absorption Coefficient

Fabrication and Properties of Porous Yttria-Stabilized Zirconia Ceramics

Two-dimensional Nucleation Growth of Stepped ZrC Skeleton with Controllable Morphology