Fabrication and Characterization of Dental Restorative Composites with Gradient Properties

Bencang Cui,Qian Ding,Fengbo Sun,Yuanhua Lin,Lei Zhang,Xuliang Deng

2020-01-01

Rare Metal Materials and Engineering

Abstract:The aim of this work was to examine the gradient mechanical properties of natural tooth and to fabricate polymer-infiltrated-ceramic network (PICN) composites for simulating natural tooth and its mechanical behaviors. The elastic modulus and Vickers hardness of enamel and dentin were examined through nano indentation. Results show that natural tooth have gradient characteristics. There are great differences in the mechanical properties of resin infiltrated partially sintered sodium aluminum silicate, alumina and zirconia. The gradient change of mechanical properties is realized through gradually changing the ceramic component. One is nano glass phase sodium aluminum silicate-micron alpha alumina laminated composites. The sintering temperature of ceramic green body is 700 degrees C. The holding time is 2, 4 and 6 h. Flexural strength, fracture toughness, elastic modulus and hardness of the composite were tested, and results show that elastic modulus and hardness of the sodium aluminum silicate-alumina composites exhibit gradient characteristics. The other is 3Y-TZP-micron alpha alumina laminated composites. The sintering temperature of green body is 1150 and 1200 degrees C, with a holding time of 2 h. The results show that both elastic modulus and hardness exhibit gradient characteristics. SEM observation shows that an interlocking grid structure is formed in transition zone. Different from ordinary homogeneous materials, composites prepared in this study have anisotropy. And therefore, the mechanical properties of the composites are closer to the primary teeth.