Synergetic impact of MgO on PMMA-ZrO2 hybrid composites: Evaluation of structural, morphological and improved mechanical behavior for dental applications
Savita Kumari,Anuj Verma,Rajat Kumar Mishra,Sarvesh Kumar Avinashi,Shweta,Shweta Singh,Priyatama Behera,Jitendra Rao,Rakesh Kumar Gautam,Bijay Laxmi Pradhan,Krishna Kishor Dey,Manasi Ghosh,Monalisa Mishra,Chandkiram Gautam
DOI: https://doi.org/10.1016/j.dental.2024.06.006
Abstract:This work aims to demonstrate the effect of ZrO2 and MgO inclusion into the Poly(methyl methacrylate) (PMMA). To fabricate novel hybrid composites via heat cure method, various composites (PZM2, PZM4 and PZM6) were synthesized in the system [(95-x) PMMA + 5 ZrO2 + x MgO] (x = 2, 4, and 6) respectively. Density of the prepared composites were determined and varying between 1.035-1.152 g/cm3. X-ray Diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) followed by EDAX and mechanical testing were performed to evaluate the fabricated composite properties. Moreover, to explore the structure of the fabricated composites the 13 C CP-MAS SSNMR and 1 H-13 C Phase-Modulated Lee Goldberg (PMLG) HETCOR Spectrum were recorded which clarify chemical shifting and motional dynamics of the composites. Mechanical tests were performed by UTM and the obtained parameters such as compressive strength, Young's modulus, fracture toughness, brittleness coefficient, flexural strength and flexural modulus are found to be in the range of 91-100 MPa, 0.48-0.51 GPa, 9.122-9.705 MPa.m1/2, 0.66-0.815, 51.03-42.78 MPa and 499-663 MPa respectively. Some more mechanical parameters such as proportional limit, elastic limit, failure strength, modulus of resilience and modulus of toughness were also calculated. Furthermore, tribological properties were also determined and the coefficient of friction (COF) was decreased by 17.4 % and 38 % for composite PZM6 at 20 N and 40 N as compared to the composite PZM2 and the lowest wear volume of 1.55 mm3 was observed for PZM2, whereas the maximum volume loss of 5.64 mm3 is observed for composite PZM6. To check out the biocompatibility, cytotoxicity and genotoxicity of the fabricated composites the Trypan-blue assay was also performed for PZM2 and PZM6 composites. Dissection on the gut of larvae was also performed on the both composites followed by DAPI and DCFH-DA staining. Therefore, these synthesized samples can be used for the fabrication of denture materials.