Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Tribological behaviors of SiC/h-BN composite coating at elevated temperatures

Wear behavior of SiC nanowire-reinforced SiC coating for C/C composites at elevated temperatures

Tribological properties of h-BN matrix solid-lubricating composites under elevated temperatures

Tribological Behavior of SiC Coating on C/C Composites Against SiC and WC under Unlubricated Sliding

Unlubricated Wear of Si/SiC and Its Composite with Nickel Si/SiC-Ni

Dry Friction and Wear Properties of Silicon Carbide with Nickel and Titanium as Compositions

Mechanical and tribological properties of h-BN/ZrO2/SiC solid-lubricating ceramic composites

Tribological behavior of h -BN/Al 2 O 3 self-lubricating composites in extreme environments–Part I: Lubricating behavior and ultra-low friction coefficient mechanism in air environments from room temperature to 1200 °C

High Temperature Low Friction Behavior of H-Bn Coatings Against ZrO2

Tribological Behavior of H-Bn/al2o 3 Self-Lubricating Composites in Extreme Environments-Part - Part I: Lubricating Behavior and Ultra-Low Friction Coefficient Mechanism in Air Environments from Room Temperature to 1200 ° C

Influence of CePO4 on High Temperature Anti-Friction and Anti-Wear Behaviors of Nickel-Based H-Bn Composite Coatings

Tribological Behavior of Si3N4 - Hbn Ceramic Materials Against Stainless Steel under Dry Friction Condition

A Study of the SiC-L Composite Ceramics for Self-Lubrication

Elevated temperature tribological properties of a-C:Si films sputtered from SiC target in the presence of C2H2 gas

Tribological Behavior of H-Bn/al2o3 Self-Lubricating Composites in Extreme Environment-Part II: Self-lubrication and Mechanism in Water-Oxygen Environment from 300 °C to 1200 °C

In situ preparation of a SiC–TiB2 composite and its wear fracture mechanism at high temperatures

Tribological Behavior of Cu-Modified Polymer-derived SiBCN Ceramics at Elevated Temperature

Understanding wear mechanisms of TiSiCN/Zr(C)N coatings at elevated temperatures

Tribological characteristics of Si3N4-hBN ceramic materials for dry application

Microstructure and performance of (CoCrNi) 88 Al 6 Ti 6 -cBN composite coatings by high-speed laser cladding (HSLC): A novel strategy for synergizing wear-resistance and friction reduction

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings