Tribological Behavior of Si3N4 - Hbn Ceramic Materials Against Stainless Steel under Dry Friction Condition

CHEN Wei,GAO Yi-min,CHEN Can
DOI: https://doi.org/10.16078/j.tribology.2010.03.010
2010-01-01
Tribology
Abstract:The main objective of this paper is to study the tribological behavior of Si3N4-hBN composites sliding on stainless steel.Unlubricated wear tests were carried out on a MMU-5G type pin-on-disc wear tester.The results showed that the addition of hBN to Si3N4 resulted in a marked decrease of friction coefficient,from 0.95 for Si3N4 against stainless steel to 0.03 for Si3N4-30%hBN against stainless steel.Wear coefficients were below 10-4 mm3/(Nm)for all materials tested and decreased sharply with increasing volume fraction of hBN,e.g.nearly zero for Si3N4-20%hBN pin.The materials and worn surfaces as well as wear debris were characterized by means of scanning electron microscopy(SEM)and X-ray diffraction(XRD).Furthermore,the tribofilms were analyzed by using electron probe microanalysis(EPMA),laser scanning microscope(LSM),X-ray photoelectron spectroscopy(XPS).The analysis indicated that,under unlubricated condition,a tribo-oxide film containing B2O3,SiO2 and Fe2O3 was formed on the wearing surface.The tribofilm with a certain thickness protected both Si3N4-hBN pin and stainless steel disc,and lubricated the wear surfaces.
What problem does this paper attempt to address?