Durability of cutting tools with deposited ceramic–metallic coatings (Ti,Al)N – Cu and (Ti,Al)N – Ni when turning and milling steels
D. S. Belov,D. N. Klauch,I. V. Blinkov,A. I. Laptev,A. P. Demirov,,,,,
DOI: https://doi.org/10.30791/0015-3214-2023-5-37-46
2023-01-01
Physics and Chemistry of Materials Treatment
Abstract:The study shows the results of comparative resistance tests of a carbide cutting tool with (Ti,Al)N – Cu and (Ti,Al)N – Ni nanostructured arc-PVD coatings deposited on its working surfaces under conditions of continuous and interrupted cutting of 13Mn6 (09G2S) and 10Cr15Ni9Si3Nb1-SH (EP302-Sh) steels, respectively. Under milling conditions of 10Cr15Ni9Si3Nb1-SH steel, when using WC – Co (6 wt.% Co) inserts with (Ti,Al)N – Cu and (Ti,Al)N – Ni coatings, tool life increases by 3.1 and 1.7 times, respectively. When turning steel 13Mn6 using WC – Co inserts coated with (Ti,Al)N – Cu and (Ti,Al)N – Ni, tool life increases by 7.6 and 10.8 times, respectively, and cutting forces Fz, Fx, Fy decrease nearly by 20 %. This effect is determined by the presence of a nanostructure in the formed coatings, the presence of a highly hard ceramic component and ductile metal, which determine their hardness (more than 35 GPa) and fracture toughness (the relative work of plastic deformation during indentation is more than 60 %), increased tribological characteristics (friction coefficient ~ 0.5 according to comparison with uncoated carbide ~ 0.7). The study noted an increased resistance of (Ti,Al)N – Ni coatings on a hard alloy to continuous cutting of steel, which is determined by their high hardness and lower friction coefficient compared to (Ti,Al)N – Cu coatings, which are characterized by better performance in interrupted cutting operations, where the determining value of resistance is the fracture toughness.