Abstract:Lattice distortion, which is intended to increase the yield strengths of alloys, is central to alloy design. This study focuses on investigating the close connection between microstructure and mechanical properties of (CoNiV)97Al3 medium-entropy alloys (MEAs) in the as-cast and annealed states. The grain size and phase composition of the alloys were optimized by combining the large deformation cold-rolling and high temperature annealing treatment, and the toughening mechanism of the alloys was evolved. After annealing at 900 and 950°C, a small amount of diffuse B2 phase appears within the alloy, which is able to strengthen the alloy to obtain high yield strength. Since intermetallic compounds such as Ni3Al are extremely unstable, they will decompose during annealing at higher temperature (1000°C), the alloy transforms into a single FCC phase. Therefore, the as-cast and annealed (CoNiV)97Al3 alloy exhibited excellent mechanical properties, including yield strengths of 0.8–1.1GPa, ultimate tensile strengths of 1.05–1.7GPa, and an optimal elongation of 36.7%. Combined with the mechanical properties and microstructure of the as-cast and annealed (CoNiV)97Al3 MEAs, the alloy strengthening was mainly attributed to the synergistic effect of dislocations, solid solution phases, and B2 brittle precipitated phases, while the good ductility was mainly due to the annealing twins. Thus, harmonizing multiple strength/toughness mechanisms can lead to a more optimal alloy strength–plasticity equilibrium point.

Mechanical Behaviors of As-Deposited and Annealed Nanostructured Ni–Fe Alloys

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Mechanical Behaviors of Electrodeposited Bulk Nanocrystalline Metals and Alloys

Effects of Annealing and Impurities on Tensile Properties of Electrodeposited Nanocrystalline Ni

Stable Ductility of an Electrodeposited Nanocrystalline Ni–20 Wt.%fe Alloy in Tensile Plastic Deformation

Anomalous Weakened Annealing-Induced Hardening in Extremely Fine Nanograined NiFe Alloys

Effects of Current Intensity on Microstructure and Mechanical Properties of Bulk nano-crystalline Ni-Fe Alloy

Unexpected Weakened Annealing-Hardening Effect in Extremely Fine Nanograined Nife Alloys

Microstructure and Mechanical Properties of the As-Cast and Annealed CoNiV-based MEAs with Al Addition

Microstructures and Deformation Mechanisms of Cr26Mn20Fe20Co20Ni14 Alloys

Microstructure and Mechanical Properties of Nano-Grained Dual-Phase Ni-Based Alloy

Increasing the ductility of nanostructured Al and Fe by deformation

Tensile Behavior of Electrodeposited Nanocrystalline Ni

Superplasticity and Microstructure Evolution of Electrodeposited Nanocrystalline Nickel

Enhanced Tensile Ductility in an Electrodeposited Nanocrystalline Ni

Bending deformation and indentation hardness of electrochemically deposited nanocrystalline nickel-iron alloys

Microstructure and Tensile Properties of Al0.5CoCrCuFeNi Alloys Produced by Simple Rolling and Annealing

Annealing Behaviour of Electrodeposited Ni–Zr and Ni–Al Composite Coatings

High Strength and High Ductility of Electrodeposited Nanocrystalline Ni with A Broad Grain Size Distribution

The Transition of Strain Rate Sensitivity Induced by Fe Solutes in Electrodeposited Nanocrystalline Ni–Fe Alloy

Mechanical Properties Improvement of Alcrfeni2ti0.5 High Entropy Alloy Through Annealing Design and Its Relationship with Its Particle-Reinforced Microstructures