Abstract:The Ni-Al intermetallic sheets were prepared by the reaction synthesis of pure Ni and Al foils with different thickness ratios. The first stage was performed at 640 °C/20 MPa/6 h to consume Al layers, and the second stage was performed at 1200 °C/20 MPa/1 h to complete the synthesis of Ni-Al intermetallic sheets. The thickness ratios of original Ni and Al foils strongly affected the microstructure and mechanical properties of Ni-Al intermetallic sheets. When Ni/Al thickness ratio was 1:1.5 (R1:1.5), the microstructure was single-phase NiAl with bimodal grain structure, and it transformed into coarse grains dominated single-phase NiAl structure when Ni/Al thickness ratio was 1:1 (R1:1). The microstructures changed to NiAl+Ni3Al+Ni when the ratios were 1:0.63 (R1:0.63) and 1:0.25 (R1:0.25). At ambient temperature, Samples R1:0.25 and R1:0.63 had high strength, while Samples R1:1 and R1:1.5 showed serious brittleness. At high temperature, Sample R1:1 showed preferable ductility with the elongation of 61.3%, 71.4% and 101.3% at 800 °C, 900 °C and 1000 °C, respectively; Sample R1:0.63 showed the highest tensile strength, with the values of 350.3 MPa, 230.5 MPa and 140.2 MPa at 800 °C, 900 °C and 1000 °C, respectively. For the fracture at ambient temperature, Sample R1:0.25 showed a mixed fracture mode of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mainly cleavage fracture; Sample R1:1 showed a typical brittle cleavage fracture with a large number of river-like patterns; the fracture mode of Sample R1:1.5 was brittle transgranular fracture for coarse grain layers (CGLs) and intergranular fracture for fine grain layers (FGLs). At high temperature, Samples R1:1.5 and R1:1 were mixed fracture modes of dimple fracture and quasi-cleavage fracture; the fracture mode of Sample R1:0.63 was mixed quasi-cleavage and cleavage fracture; the fracture mode of Sample R1:0.25 was single cleavage fracture with microcracks at the NiAl layers.

Revealing mechanical property–strengthening micro-mechanism of Ni/Ni3Al-based alloys by molecular dynamics simulation

A Molecular Dynamics Study on Mechanical Performance and Deformation Mechanisms in Nanotwinned NiCo-based Alloys with Nano-Precipitates under High Temperatures

Molecular Dynamics Simulation of Tensile Mechanical Properties of Ni/Ni<sub>3</sub>Al

Microstructure evolution and mechanical behavior of the Ni/Ni3Al interface under thermal-mechanical coupling

Tensile Mechanical Properties of Ni-Based Superalloy of Nanophases Using Molecular Dynamics Simulation

Microstructure and Mechanical Properties of the As-Cast and Annealed CoNiV-based MEAs with Al Addition

Temperature Effects on Deformation Substructures and Mechanisms of a Ni-based Single Crystal Superalloy

Tensile Mechanical Properties of Ni3Al Nanowires at Intermediate Temperature

Orientation dependence of microstructure deformation mechanism and tensile mechanical properties of Nickel-based single crystal superalloys: A molecular dynamics simulation

Molecular Dynamics Simulation and Mechanical Properties Analysis of Ni-Fe Alloy under Uniaxial Stretching

Micro-alloying effects of Ni on the microstructure and mechanical properties of an Al-Zn-Mg-Cu-Sc-Zr alloy

Microstructures and Mechanical Properties of NiTiFeAlCu High-Entropy Alloys with Exceptional Nano-precipitates

Microstructures and Deformation Mechanisms of Cr26Mn20Fe20Co20Ni14 Alloys

Microstructural evolution and mechanical properties of Ni/Al reactive nanolaminates with different NixAly intermetallic phases

Regulating microstructures and mechanical properties of Al-Fe-Ni alloys

The deformation behavior and mechanism modeling of a corrosion-resistant Ni-Cr-Mo alloy with nanoscale precipitates at room and elevated temperatures

Microstructure and Mechanical Properties at Elevated Temperature of Mg-Al-Ni Alloys Prepared Through Powder Metallurgy

Microstructures and Mechanical Behaviors of NiAlFe Intermetallic Compounds

Effects of the Temperature, Strain Rate, and Loading Conditions on the Deformation Behaviors and Mechanical Properties of the Ni/Ni3Al Superalloy

The microstructure and mechanical properties of reaction synthesized Ni-Al intermetallic sheets by pure Ni/Al foils with different thickness ratios

Molecular dynamics simulation of the ' phase deformation behaviour in nickel-based superalloys